[1]韩　军,高惠临,韩新利.HFW钢管焊缝疲劳特性与疲劳寿命预测方法研究[J].焊管,2011,34(12):27-31.[doi:1001-3938（2011）12-0027-06]
　HAN Jun,GAO Hui-lin,et al.Research on the Fatigue Property of HFW Pipe Welded Seam and Fatigue Life Forecast Method[J].,2011,34(12):27-31.[doi:1001-3938（2011）12-0027-06]
点击复制

HFW钢管焊缝疲劳特性与疲劳寿命预测方法研究
分享到：

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
34
期数:
2011年第12期
页码:
27-31
栏目:
试验与研究
出版日期:
2011-12-28

文章信息/Info

Title:
Research on the Fatigue Property of HFW Pipe Welded Seam and Fatigue Life Forecast Method
文章编号:
1001-3938（2011）12-0027-06
作者:
韩　军1; 2 ; 高惠临1 ; 韩新利2
（1. 西安石油大学，西安 710065；
2. 中国石油集团石油管工程技术研究院，西安 710065）
Author(s):
HAN Jun1;  2;  GAO Hui-lin1;  HAN Xin-li2
（1.Xi’an Petroleum University, Xi’an 710065, China;
2. CNPC Tubular Goods Research Institute, Xi’an 710065, China）
关键词:
HFW钢管焊缝; 疲劳特性; 疲劳寿命预测; Miner线性累计损伤模型
Keywords:
HFW pipe welded seam;  fatigue property;  fatigue life forecast;  Miner linear cumulative damage model
分类号:
TG115.5
DOI:
1001-3938（2011）12-0027-06
文献标志码:
A
摘要:
受停输启用和供需变动的影响，油气管道的输送压力会发生周期性的变化，疲劳失效问题异常突出。特别是对于含有裂纹缺陷的管道，在疲劳载荷的作用下，若管道的应力强度因子幅超过疲劳裂纹扩展门槛值，裂纹就会发生疲劳扩展。当裂纹扩展到一定程度，超过管道运行压力下所能承受的临界缺陷极限尺寸，管道就会发生疲劳失效，从而影响到管道的使用寿命。采用高频疲劳试验机测试了X80钢级HFW焊管焊缝的疲劳裂纹扩展门槛值与疲劳裂纹扩展速率，结合API 579《适用性评价规范》中推荐的失效评估图技术（FAD）和Miner线性疲劳损伤积累理论，考虑了多种应力比对管道疲劳寿命的影响，建立了双参数HFW管道的疲劳寿命预测方法。
Abstract:
The transportation pressure of oil and gas pipeline can change periodically because of restart and supply change, so the fatigue failure problems stand out exceptionally. Especially for pipeline with crack defect, when the value of stress intensity factor exceeds fatigue crack expansion threshold value under fatigue load, the crack will expand; when crack expansion exceed critical defect extreme dimension under pipeline operation pressure, the fatigue failure of pipeline will happen, this will affect useful life of pipeline. In this article, the fatigue crack expansion threshold value of X80 HFW pipe welded seam and fatigue crack propagation rate were tested by using high-frequency fatigue testing machine, combined with the failure assessment diagram(FAD) recommended in API 579 Fitness-for-service Specification and the Miner’s linear cumulative damage theory, considering the effect of combined stress ratio on pipeline fatigue life, the fatigue life forecast method for two-parameter HFW pipeline was established.

参考文献/References:

［1］ 周惠久，黄明志. 金属材料强度学［M］. 北京: 科学出版社，1989.
［2］ RITCHIE R O， GILBERT C J，MCNANET J M. Mechanics and Mechanisms of Fatigue Damage and Crack growth in Advanced Materials ［J］. International Journal of Solids and Structures， 2000（37）： 311-329.
［3］ FERRERIA J M， PEREIRA A H， BRANCO C M. A Fracture Mechanics Based Fatigue Life Prediction for Welded Joints of Square Tubes［J］. Thin-Walled Structures，1995（21）：107-120.
［4］ IBS J B，AGERSKOV H. An Analytical Model for Fatigue Life Prediction Based on Fracture Mechanics and Crack Closure［J］. Construct Steel Research， 1996 （37）： 229-261.
［5］ 罗金恒， 赵新伟， 熊庆人，等. 缺陷管道疲劳寿命预测新模型及试验验证［J］. 石油机械， 2005， 33（2）：5-7.
［6］ 刁顺， 冯耀荣， 庄传晶，等. 几种油气输送管材料的疲劳特性与管道寿命预测［J］. 中国安全科学学报， 2008 （1）：123-130.
［7］ 袁大伟. ERW焊管焊缝冲击韧性的影响因素分析［J］. 焊管， 2008， 31（3）:67-70.
［8］ 赵坤. 浅谈ERW钢管错边缺陷［J］. 焊管， 2008， 31（2）:67-68.
［9］ 史福忠， 马建国， 陈燕军. ERW焊管焊缝热影响区性状与焊管质量的相关性初探［J］. 焊管， 2007， 30（3）：60-62.

备注/Memo

备注/Memo:
韩 军（1980—），男，河北行唐人，在读硕士研究生，工程师，主要从事石油管材质量监督检验和试验研究工作。
更新日期/Last Update: