[1]尹 燕,郑祥超,陈 燕,等.背面保护剂对304不锈钢焊接接头腐蚀性能的影响[J].焊管,2012,35(5):19-22.[doi:１００１－３９３８（２０１２）０5-0019-04]
　YIN Yan,ZHENG Xiang-chao,CHEN Yan,et al.Influence of Back Protective Agent on the Corrosion Properties of 304 Stainless Steel Welded joints[J].,2012,35(5):19-22.[doi:１００１－３９３８（２０１２）０5-0019-04]
点击复制

背面保护剂对304不锈钢焊接接头腐蚀性能的影响
分享到：

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
35
期数:
2012年第5期
页码:
19-22
栏目:
试验与研究
出版日期:
2012-05-28

文章信息/Info

Title:
Influence of Back Protective Agent on the Corrosion Properties of 304 Stainless Steel Welded joints
文章编号:
１００１－３９３８（２０１２）０5-0019-04
作者:
尹 燕; 郑祥超; 陈 燕; 张为山; 张瑞华
（兰州理工大学 甘肃省有色金属新材料省部共建国家重点实验室，兰州 730050）
Author(s):
YIN Yan;  ZHENG Xiang-chao;  CHEN Yan;  ZHANG Wei-shan;  ZHANG Rui-hua
（State Key Laboratory of Gansu Advanced Non-ferrous Metal Materials， Lanzhou University of Technology，Lanzhou 730050，China）
关键词:
不锈钢焊接; 氯离子; 保护剂; 焊缝; 腐蚀性能
Keywords:
stainless steel welding;  chloride ion;  protective agent;  weld;  corrosion property
分类号:
TG441.4
DOI:
１００１－３９３８（２０１２）０5-0019-04
文献标志码:
A
摘要:
采用兰州理工大学自行研制的不锈钢背面保护剂，通过对比试验，在使用背面保护剂和不使用背面保护剂两种情况下，配置符合标准的FeCl3和HCl的混合溶液，对不锈钢焊缝进行氯离子腐蚀试验。结果表明，使用背面保护剂的试样背面未被氧化的，呈银白色金属光泽，余高适中，表面光滑，且不锈钢焊缝腐蚀率小；未使用背面保护剂的不锈钢试样焊缝背面氧化严重，表面形成一层“黑皮”，成形不好且腐蚀率大。不锈钢焊接使用背面保护剂可以有效改善焊缝的背面成形、提高焊缝对氯离子的耐腐蚀性能。
Abstract:
In this article， chloride ion corrosion tests were conducted in standard ferric chloride and hydrochloric acid mixture ， by using or without using stainless steel back protective agent which was self-developed. The result indicated that using specimen with back protective agent can receive silvery white weld with smooth surface， suitable reinforcement and low corrosion rate； the weld of stainless steel specimen without using back protective agent oxidized severely， and a black skin formed in weld surface， the weld formation was not good and with high corrosion rate. Using back protective agent can effectively improve weld formation and increase corrosion resistance to chloride ion in stainless steel welding.

参考文献/References:

［1］ ZHANG R H， FAN D. Numerical Simulation of Effects of Activating Flux on Flow Patterns and Weld Penetration in ATIG Welding［J］. Science and Technology of Welding and Joining，2007，12（01）：15-23.
［2］ 张瑞华，樊丁，余淑荣.低碳钢A-TIG焊的活性剂研制 ［J］.焊接学报，2003，24（02）：16-18.
［3］ 张瑞华，尹燕，水谷正海，等.A-TIG焊接熔池行为的观察［J］.机械工程学报，2009，45（03）：115-118.
［4］ 张瑞华，樊丁.低碳钢A-TIG焊活性剂的焊接性［J］.焊接学报，2003，24（01）：85-87.
［5］ 吴军，魏群，卞伟.T91_TP304钢用免充氩焊接保护剂性能测试［J］.山东电力技术，2006（01）：30-32.
［6］ 王偐，段云春，吕龙.背面免充氩气保护剂在不锈钢焊接中的应用［J］. 现代焊接，2008，61（01）：43-44
［7］ 王敬红.T/P91钢焊接时的背面气体保护技术［J］.焊接，2001（06）：36-37.
［8］ 杨丽娟，唐吉威.锅炉压力容器制造常用背面保护方法探讨［J］.电站系统工程，2008（01）：73.
［9］ 秦惠中，郝世英，石 凯，等.埋弧焊陶质衬垫单面焊双面成型技术研究［J］.石油工程建设，2001（08）：17-18.
［10］ 李国栋.不锈钢单面焊接头性能及背面保护机理的研究［D］.北京：北京工业大学，2005.

备注/Memo

备注/Memo:
作者简介：尹 燕（1973—），女，四川西昌人，副教授，主要从事激光加工及新型功能材料制备与表征等研究工作。
更新日期/Last Update: