[1]马家鑫,皇甫严凯,杨专钊,等.油气输送钢管硫化物应力腐蚀开裂试验评定标准探讨[J].焊管,2013,36(3):61-64.[doi:1001-3938(2013)03-0061-04]
 MA Jiaxin,HUANGFU Yankai,YANG Zhuanzhao,et al.Discussion on Evaluation Standards for Sulfide Stress Corrosion Cracking in Oil & Gas Transmitting Pipeline[J].,2013,36(3):61-64.[doi:1001-3938(2013)03-0061-04]
点击复制

油气输送钢管硫化物应力腐蚀开裂试验评定标准探讨
分享到:

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
36
期数:
2013年第3期
页码:
61-64
栏目:
标准化
出版日期:
2013-03-28

文章信息/Info

Title:
Discussion on Evaluation Standards for Sulfide Stress Corrosion Cracking in Oil & Gas Transmitting Pipeline
文章编号:
1001-3938(2013)03-0061-04
作者:
马家鑫12皇甫严凯2杨专钊12李记科12李云龙12
(1.中国石油集团石油管工程技术研究院,西安 710065;
2.北京隆盛泰科石油管科技有限公司,北京 100101)
Author(s):
MA Jiaxin12 HUANGFU Yankai2 YANG Zhuanzhao 12 LI Jike 12 LI Yunlong 12
(1.CNPC Tubular Goods Research Institute,Xi’an 710065,China;
2.Beijing Longshine Oil Tubular Technology Co.,Ltd.,Beijing 100101,China)
关键词:
关键词:油气输送管硫化物应力腐蚀开裂标准
Keywords:
Key words: oil & gas transmitting pipeline sulfide stress corrosion cracking(SSCC) standard
分类号:
TE988.2
DOI:
1001-3938(2013)03-0061-04
文献标志码:
B
摘要:
对国内外金属硫化物应力腐蚀开裂试验的标准、评定指标进行了概述及总结,分析了油气输送管用硫化物应力腐蚀开裂试验中试验标准选择时应注意的问题,并参照国内外SSCC试验常用相关标准,建议将NACE TM 0177《含H2S 环境中金属抗特定的环境开裂的实验室试验》方法和ASTM G39《弯梁应力腐蚀试验试件的制备和使用的标准方法》相结合,并借鉴ASTM和NACE的做法,采用临界应力值判断和试样外观宏观及微观检测相结合的方法作为评定指标。
Abstract:
The standards and the evaluation index of the sulfide stress corrosion cracking(SSCC) test in China domestic and the abroad were summarized, and the problems should be paid attention to selecting test standard for SSCC were analyzed. Refer to the related standards commonly used in SSCC test in China domestic and the abroad, it suggests adopting NACE TM 0177 Laboratory Testing of Metals for Resistance to Sulfide Stress Cracking and Stress Corrosion Cracking in H2S Environments Item and ASTM G39 Stress Corrosion Testing-preparation and Use Bent-beam Specimens. Combined with ASTM and NACE, it can combine critical stress judgment and macroscope as well as microscope testing of specimen surface to regard as assessment index.

参考文献/References:

[1] 邵晓东,庄传晶,韩新利,等.酸性环境用油气输送管线钢的研究进展[J].机械工程材料,2010,34(11):1-4,78.
[2] 李云涛.国产X70管线钢及其焊接接头的硫化氢腐蚀性能研究[D].天津:天津大学,2003.
[3] 张亮,李晓刚,杜翠薇,等.管线钢应力腐蚀影响因素的研究进展[J] .腐蚀科学与防护技术,2009,21(01):62-65.
[4] 左景伊.应力腐蚀破裂[M].西安:西安交通大学出版杜,1985.
[5] 米秋占,于英姿.输气管道的硫化物应力腐蚀(SSCC)问题[J].焊管,2000(09):6-9.
[6] ISO 15156-1,石油天然气工业-石油和天然气生产中含H2S环境使用的材料-选择抗裂纹材料的一般原则[S].
[7] API SPEC 5L,管线钢管规范(第44版)[S].

相似文献/References:

[1]仝 珂,韩新利,宋 寰,等.L245NS抗硫弯管力学性能及HIC 和SSC试验分析[J].焊管,2012,35(12):45.[doi:1001-3938(2012)12-0045-05]
 TONG Ke,HAN Xinli,SONG Huan,et al.Mechanical Property, HIC and SSC Test Analysis of L245NS Anti-Sulfur Bending Pipe[J].,2012,35(3):45.[doi:1001-3938(2012)12-0045-05]
[2]王 军,毕宗岳,张 峰,等.SEW高抗挤套管开发[J].焊管,2014,37(2):18.
 WANG Jun,BI Zongyue,ZHANG Feng,et al.R&D of SEW High Collapse Resistance Oil Casing[J].,2014,37(3):18.

备注/Memo

备注/Memo:
—————————
作者简介:马家鑫(1987—),男,硕士学位,助理工程师,现从事石油管工程技术服务与科研工作。
更新日期/Last Update: