核电机组主管道焊缝返修技术及应用
分享到：

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
38
期数:
2015年第8期
页码:
29-33
栏目:
应用与开发
出版日期:
2015-08-28

文章信息/Info

Title:
Weld Repair Technology and Application of Nuclear Power Unit Main Pipeline
文章编号:
１００１－３９３８（２０１5）08-0029-05
作者:
尚 巍1; 薛敬凯1; 刘铖丹1; 王永新2
1. 中国核动力研究设计院核燃料及材料研究所， 成都 610213；
2. 秦山核电有限公司， 浙江 嘉兴 214300
Author(s):
SHANG Wei;  XUE Jingkai;  LIU Chengdan;  WANG Yongxin
1. Nuclear fuel and material research institute of Unclear Power Institute of China, Chengdu 610213, China;
2. Qinshan Unclear Power Co., Ltd., Jiaxing 214300, Zhejiang, China
关键词:
核电机组; 主管道焊缝; 焊接缺陷; 返修
Keywords:
nuclear power unit;  main pipeline weld;  welding defects;  repair
分类号:
TG47
DOI:
１００１－３９３８（２０１5）08-0029-05
文献标志码:
B
摘要:
主管道在核电站安全中起着至关重要的作用，主管道焊接质量也显得尤为重要。在目前核电机组主管道焊接中，窄间隙自动焊逐渐取代了传统的手工焊，提高了焊接效率。但由于主管道窄间隙自动焊采用单层单道焊接工艺，如果控制不好，容易出现未熔合等缺陷，影响焊缝质量，必须进行返修。以方家山核电工程2#机组主管道返修过程为例，介绍了一种成功应用于工程实践的主管道手工返修工艺，并归纳总结了主管道自动焊接缺陷类型、产生的原因及返修方法。
Abstract:
Main pipeline plays an important role in nuclear power plant safety, and main pipeline welding quality also is very important. In main pipeline welding of the current nuclear power units, narrow gap automatic welding gradually replaced the traditional manual welding, which improved the welding efficiency. But it used single-layer single-channel welding process in main pipeline narrow gap automatic welding, if the control is not good, some defects easily appear such as incomplete fusion, affect the weld quality, must be repaired. Taking repair process of Fangjiashan nuclear power project 2# unit main pipeline as example, it introduced a kind of main pipeline manual repair process which successfully used in engineering practice, and summarized welding defects type of main pipeline, causes and repair methods.

参考文献/References:

［1］张雯，梁健，谭文良，等. CPR1000核岛主管道自动焊效益分析[J]. 科技创新导报，2013（8）: 123-126.
［2］吕旭伟，马立民，朱德才，等. 核电站主管道自动焊焊缝缺陷的返修研究[J]. 科技创新导报，2012（35）：2-3.
［3］GB/T 8923.3—2009，焊缝、边缘和其他区域的表面缺陷的处理等级[S].
［4］吴晓清，张连生. 熔焊原理[M]. 北京：机械工业出版社，1994.
［5］成大先. 机械设计手册[M]. 北京：机械工业出版社，2008.
［6］陈祝年. 焊接工程师手册[M]. 北京：机械工业出版社，2010.
［7］王洪光. 实用焊接工业手册[M]. 北京：化学工业出版社，2014.
［8］王洪光. 实用焊接设备手册[M]. 北京：化学工业出版社，2012.
［9］陈勇. 常用焊接材料速查手册[M]. 北京：机械工业出版社，2011.
［10］ 中国机械工程学会焊接学会. 焊接手册[M]. 北京：机械工业出版社，2008.

备注/Memo

备注/Memo:
收稿日期：2014-11-30
修改稿收稿日期：2015-07-17
作者简介: 尚   巍（1988—），男，硕士研究生，主要研究方向为焊接工艺。
更新日期/Last Update: