TA1/X65复合板对焊工艺及焊缝组织和性能分析
分享到：

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
39
期数:
2016年第10期
页码:
30-34
栏目:
工艺与设备
出版日期:
2016-10-28

文章信息/Info

Title:
Analysis on the Butt Welding Process of TA1/X65 Composite Plates and
Weld Microstructure and Properties
文章编号:
DOI: 10.19291/j.cnki.1001-3938.2016.10.008
作者:
杨 军1; 2;  关尚虎3;  田 磊1; 2;  张 超1; 2;  宋红兵1; 2
1. 国家石油天然气管材工程技术研究中心， 陕西 宝鸡 721008；
2. 宝鸡石油钢管有限责任公司 钢管研究院， 陕西 宝鸡 721008；
3. 天水天力特种管有限公司， 甘肃 天水 741020
Author(s):
YANG Jun1;  2;  GUAN Shanghu3;  TIAN Lei1;  2;  ZHANG Chao1;  2;  SONG Hongbing1;  2
1. National Engineering Technology Research Center for Petroleum and Natural Gas Tubular Goods， Baoji 721008, Shaanxi, China；
2. Steel Pipe Research Institute of Baoji Petroleum Steel Pipe Co., Ltd., Baoji 721008, Shaanxi, China；
3. Tianshui Tianli Special Steel Pipe Co., Ltd., Tianshui 741020， Gansu，China
关键词:
TA1/X65复合板; MAG+TIG焊接; 金属间化合物; 焊接热输入
Keywords:
TA1/X65 composite plates;  MAG+TIG welding;  intermetallics;  welding heatinput
分类号:
TG457.1
DOI:
DOI: 10.19291/j.cnki.1001-3938.2016.10.008
文献标志码:
A
摘要:
为了提高钛/钢复合板对焊接头性能，选择3种工艺方案进行焊接试验，采用金相显微组织分析、显微硬度和焊缝背弯试验，研究了钛/钢复合板对接焊缝组织特征、显微硬度分布及焊缝背弯性能。结果表明，工艺方案3成功实现了薄覆层钛/钢复合板对焊连接，焊接接头背弯角度可达100°，拉伸面完好，焊缝性能达到项目预期指标要求。钛覆层搭接焊质量严重影响复合板对焊接头全壁厚背弯性能。钛焊缝区显微组织为锯齿状α-Ti+针状α-Ti+晶界β-Ti，热影响区组织为多形态粗大α-钛。显微硬度较高区域出现在钛焊缝熔敷金属区，硬度值达200HV10。精确控制熔深、降低热输入、减小热影响区尺寸及细化晶粒，是提高钛焊缝塑韧性和安全可靠性的有效方法。
Abstract:
In order to enhance the performance of butt welded joint on titanium/steel composite plate and discuss reasonable process design， the microstructure character， microhardness distribution and mechanical properties of butt welds were investigated by using optical microscopy， microhardness and back bending tests. The results indicated that the process plan 3 in this paper successfully implemented butt welding of the thin coated titanium/steel composite plate， the back welding angle of butt welded joint reached 100°， the tensile surface was intact， and the performance of the weld met the expected requirements of the project. The overlap welding quality of titanium clad seriously affected the back welding performance of full-thickness samples on welded joint. The microstructure of TA1 welded joint was consisted of jagged α-Ti， acicular α-Ti and grain boundary β-Ti， and polymorphic coarse α-Ti existed in the HAZ.  The high hardness region of titanium clad appeared in the deposited weld area， the hardness was 200HV10 . Therefore， it is an important method of precise control depth of fusion， lower heat input， reduce the size of HAZ and grain refinement to improve the toughness and security of the titanium weld.

参考文献/References:

[1] 张喜燕，白晨光，赵永庆. 钛及钛合金的应用[M]. 北京：机械工业出版社，2005：287-288.
[2] YUAN X J，SHENG G M，QIN B. Impulse pressuring diffusion bonding of titanium alloy to stainless steel[J]. Materials Characterization，2008，59（7）：930-936.
[3] 张克华，董定元. 钛及钛合金的焊接[M]. 北京：机械工业出版社，1985：83-84.
[4] 盛长城. 钛合金厚板窄间隙手工TIG焊接工艺和性能研究[D]. 江苏：江苏科技大学，2008.
[5] 张杭永，郭新虎，刘继雄，等. 大面积钛/钢复合板的爆炸焊接工艺及其组织与性能研究[J]. 中国钛业，2013（3）：27-30.
[6] 王廷，张秉刚，陈国庆，等. 钛/钢异种金属焊接存在问题及研究现状[J]. 焊接，2009（9）：29-33.
[7] 杨军，毕宗岳，牛辉，等. TA1/X65复合板焊接工艺及焊缝组织性能研究[J]. 焊管，2015（6）：1-10.
[8] 李鹏，李京龙，熊江涛，等. TA2/Ni+Nb中间层/1Cr18Ni9Ti扩散焊接头的组织与性能[J]. 航空材料学报，2010，30（5）：25-29.
[9] 李国庆. 小直径TA2钛管氩弧焊焊接[J]. 焊管，2011（11）：39-41.
[10] 刘鹏，陆明，冀鑫炜，等. 钛/钢复合板爆炸焊接装药厚度下限研究[J]. 兵器材料科学与工程，2011，34（3）：14-17.
[11] 毕宗岳，杨军，刘海璋，等. TA1/X65复合板焊接工艺及焊缝组织和性能研究[J]. 金属学报，2016，52（8）：1017-1024.
[12] 闫伟. Ti-55钛合金板材的CO2激光焊与电子束焊的实验研究[D]. 沈阳：东北大学，2006.
[13] MIRIYEV A，STERN A，TUVAL E，et al. Titanium to steel joining by spark plasma sintering（sps） technology[J]. Journal of Materials Processing Technology，2013， 213（2）：161-166.
[14] GB/T 13149—2009，钛及钛合金复合板焊接技术要求[S].
[15] 斯重遥，周振丰，张延生. 焊接金相图谱[M]. 北京：机械工业出版社，1987.

备注/Memo

备注/Memo:
收稿日期： 2016－03－07
基金项目： 国家863计划项目“双金属层状结构复合管材技术研究”（项目号2013AA031303）。
作者简介： 杨   军（1982—）， 男， 陕西汉中人， 工程师，硕士， 研究方向为油气管材开发及异种材料焊接技术。
更新日期/Last Update: