[1]张彦文,张友登,王志奋,等.煤气瓶耐压试验漏气原因分析[J].焊管,2017,40(6):65-68.[doi:10.19291/j.cnki.1001-3938.2017.06.012]
　ZHANG Yanwen,ZHANG Youdeng,WANG Zhifen,et al.Leakage Cause Analysis of Gas Cylinder Withstand Pressure Test[J].,2017,40(6):65-68.[doi:10.19291/j.cnki.1001-3938.2017.06.012]
点击复制

煤气瓶耐压试验漏气原因分析
分享到：

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
40
期数:
2017年第6期
页码:
65-68
栏目:
经验交流
出版日期:
2017-06-28

文章信息/Info

Title:
Leakage Cause Analysis of Gas Cylinder Withstand Pressure Test
文章编号:
10.19291/j.cnki.1001-3938.2017.06.012
作者:
张彦文1; 张友登1; 王志奋1; 陶 勇2
1. 武汉钢铁（集团）公司研究院， 武汉430080；
2. 武钢股份有限公司质检中心， 武汉430080
Author(s):
ZHANG Yanwen1;  ZHANG Youdeng1;  WANG Zhifen1;  TAO Yong2
1. Research and Development Center of Wuhan Iron and Steel Company, Wuhan 430080, China；
2. Quality Inspection Center of Wuhan Iron and Steel Company, Wuhan 430080, China
关键词:
煤气瓶; 漏气; 剪切; 裂纹
Keywords:
gas cylinder;  air leakage;  shearing;  crack
分类号:
TE972.1
DOI:
10.19291/j.cnki.1001-3938.2017.06.012
文献标志码:
B
摘要:
为了探究某HP295钢制煤气瓶耐压试验漏气原因，对漏气煤气瓶进行了宏观观察，找出漏气部位，采用扫描电镜观察、金相分析等方法对缺陷部位进行了分析。结果显示，漏气部位均位于瓶腰焊缝附近，对于制瓶的冲压钢板而言，开裂部位位于钢板的剪切边；裂纹周围未观察到聚集分布的夹杂物及脱碳现象，缺陷部位及正常部位组织均为铁素体+珠光体。分析表明，原料钢板剪切开裂及试压漏气是由剪切设备故障导致剪切边存在较长裂纹造成，应及时对剪切设备进行检修维护，保持设备正常工作状态，避免剪切边产生较长裂纹。
Abstract:
In order to explore the leakage reason of HP295 steel gas cylinder withstand pressure test, the macroscopic observation of leakage gas cylinder was conducted, found the leakage point. It adopted the methods of scanning electron microscope, metallographic analysis and so on to analyze defective parts. The results showed that the leakage parts located near the weld of cylinder waistline, and the cracking area of the stamping cracking plate also located in the shear edge of steel plate; the aggregated distribution inclusions and decarburization were not be observed around the cracks, and microstructure of defect locations and normal locations both were ferrite and perlite. The analysis results indicated that the raw material steel plate shear crack and pressure testing leakage caused by the long crack in shear edge, which caused by shear equipment failure. It should timely conduct repair and maintenance to shear equipment, so as to keep normal working state of equipment and avoid generating long cracks in shearing edge.

参考文献/References:

[1] 李义皖. 冲压加工中模具磨损的原因及预防[J]. 锻压技术, 1998（6）: 58-59.
[2] 张武彬, 柴毅忠, 李轲新, 等.气瓶钢HP295深冲后出现裂纹的原因分析及改进措施[J]. 河南冶金, 2007, 15（S1）:31-32.
[3] 陈兴福, 杨同利, 肖继明, 等. HP295开裂原因分析及改进措施[J]. 钢铁钒钛, 2012, 33（5）: 70-74.
[4] 赵东, 王立群.? 钢板剪切边开裂原因分析及改进剪切质量的措施[J]. 山东冶金，2007, 29（2）: 37-39.
[5] 高锦国, 李京社, 唐海燕, 等. 气瓶钢中非金属夹杂物研究[J]. 钢铁钒钛, 2008, 29（3）: 17-21.
[6] 潘国平, 王小燕, 后宗保. 国内热轧焊接气瓶钢的质量现状[J]. 安徽冶金, 2003, 41（4）: 15-19.
[7] 尹训强, 尚超. 提高钢板剪切质量的工艺研究及生产应用[J]. 科技信息, 2010（18）: 382.
[8] 刘建磊. 提高钢板剪切精度[J]. 宽厚板, 2002, 8（1）:? 22-24.
[9] 田正宏, 田青超, 冯长宝, 等. 热轧高强度钢板剪切开裂原因[J]. 理化检验: 物理分册, 2008, 44（10）: 571-574.

备注/Memo

备注/Memo:

作者简介： 张彦文（1972—）， 男， 湖北孝感人， 博士， 教授级高工，主要从事金属材料失效分析工作，发表论文40余篇。

收稿日期： 2017-03-10

更新日期/Last Update: