[1]刘玉栋,等.电弧喷涂Fe-Al涂层的摩擦磨损行为[J].焊管,2018,41(2):10-13.[doi:10.19291/j.cnki.1001-3938.2018.02.003]
 LIU Yudong,ZHOU Yong,WANG Meng,et al.Friction and Wear Behavior of Arc Spraying Fe-Al Coating[J].,2018,41(2):10-13.[doi:10.19291/j.cnki.1001-3938.2018.02.003]
点击复制

电弧喷涂Fe-Al涂层的摩擦磨损行为()
分享到:

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
41
期数:
2018年第2期
页码:
10-13
栏目:
试验与研究
出版日期:
2018-02-28

文章信息/Info

Title:
Friction and Wear Behavior of Arc Spraying Fe-Al Coating
文章编号:
10.19291/j.cnki.1001-3938.2018.02.003
作者:
刘玉栋1 2周 勇3王 猛3田小江1 2唐家睿1 2
1. 国家石油天然气管材工程技术研究中心, 陕西 宝鸡 721008;
2. 宝鸡石油钢管有限责任公司, 陕西 宝鸡 721008;
3. 西安石油大学 材料科学与工程学院, 西安 710065
Author(s):
LIU Yudong12 ZHOU Yong3 WANG Meng3 TIAN Xiaojiang12 TANG Jiarui12
1. Chinese National Engineering Research Center for Petroleum and Natural Gas Tubular Goods, Baoji 721008, Shaanxi, China;
2. Baoji Petroleum Steel Pipe Co., Ltd., Baoji 721008, Shaanxi, China;
3. College of Materials Science and Engineering, Xi’an Shiyou University, Xi’an 710065, China
关键词:
关键词:Fe-Al涂层超音速电弧喷涂金属间化合物摩擦磨损
Keywords:
Fe-Al coating supersonic arc spraying intermetallic compound friction and wear
分类号:
TG174.2
DOI:
10.19291/j.cnki.1001-3938.2018.02.003
文献标志码:
A
摘要:
为了研究Fe-Al涂层的组织结构,并比较其与20#钢的耐磨性能,采用粉芯丝材和超音速电弧喷涂技术在20#钢基体上制备了Fe-Al涂层,采用扫描电镜分析了涂层的组织形貌,用X射线衍射分析了涂层的相结构,并对比研究了涂层与20#钢在干摩擦条件下的耐磨损性能。研究结果表明,采用超音速电弧喷涂制备的Fe-Al涂层组织致密,与基体结合良好,具有较高的硬度,在相同载荷和转速下,Fe-Al涂层的摩擦系数较小,具有优异的耐磨性。
Abstract:
In order to research the structure of Fe-Al coating and compare the abrasion resistance with 20# steel, the Fe-Al coatings were prepared on 20# steel substance by supersonic arc spraying, the surface morphologies of Fe-Al coatings were analyzed by SEM. the phase structure of the coating were analyzed by X-ray diffraction, and the abrasion resistance of coating and 20# steel substrate were studied and compared under the condition of dry friction. The results showed that Fe-Al coating was fully dense with low porosity, higher microhardness and well bonding with substrate. In the same load and revolving speed, the friction coefficient of Fe-Al coating was lower and the abrasion resistance was better.

参考文献/References:

[1] 尹衍升, 张金升, 李嘉, 等. 新型半陶瓷材料-金属间化合物及其应用[J]. 中国陶瓷, 2002, 38(1): 39-42.
[2] 栗卓新, 方建筠, 史耀武, 等. 高速电弧喷涂Fe-TiB2/Al2O3复合涂层的组织及性能[J]. 中国有色金属学报,2005(11): 154-159.
[3] 张建民, 仲增墉, 张瑞林, 等. Fe-Al系金属间化合物本征脆性的电子理论[J]. 材料研究学报, 1996, 10(3):230-234.
[4] 孙祖庆, 黄原定, 杨王玥, 等. Fe3Al基金属间化合物合金强韧化途径探索[J]. 金属学报, 1993, 29(8): 20-24.
[5] 丁彰雄, 陈江涛, 王群. FeCrAl合金涂层抗高温氧化及热腐蚀性能研究[J].武汉理工大学学报(交通科学与工程版), 2003(4): 513-516.
[6] BANOVIC S W, DUPONT J N ,MARDER A R. Experimental evaluation of Fe-Al claddings in high-temperature sulfdising environments[J]. Welding Researeh,2001(3): 63-70.
[7] 赵雁潮, 魏琪, 栗卓新, 等. 热喷涂技术在锅炉管道防护中的应用进展[J]. 材料保护, 2006(8):43-46,73.
[8] 许思勇, 晖云, 张永俐. 电弧喷涂技术的发展及应用[J].云南冶金, 2002, 31(3): 138-141, 157.
[9] 刘广海. 电弧喷涂技术的发展现状及其在主要工业领域的应用[J]. 金属加工(热加工), 2008 (18): 26-29.
[10] 张亚梅, 李午申, 冯灵芝, 等. 电弧喷涂技术的现状与发展[J]. 焊接, 2003(10): 5-8.
[11] KAISER J J, MILLER R A. Inert gas improves arc sprayed coatings[J]. Advanced Materials & Processes,1989 (12): 37-40.
[12] 王有喜, 张勇, 张春明, 等. 电弧喷涂技术的发展及应用[J]. 农业装备与车辆工程, 2010(3): 26-29.

备注/Memo

备注/Memo:

收稿日期: 2017-11-06

作者简介: 刘玉栋(1988—), 男, 硕士, 助理工程师, 主要从事石油管材工程试验与检测评价工作。

更新日期/Last Update: 2018-03-22