[1]黄晓辉,等.内壁淬火硬化合金管组织性能研究[J].焊管,2018,41(4):19-23.[doi:10.19291/j.cnki.1001-3938.2018.04.004]
　HUANG Xiaohui.,LI Huabin,NIU Aijun.,et al.Study on Microstructure and Properties of Alloy Pipe with Inner Wall Quench Hardening[J].,2018,41(4):19-23.[doi:10.19291/j.cnki.1001-3938.2018.04.004]
点击复制

内壁淬火硬化合金管组织性能研究()
分享到：

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
41
期数:
2018年第4期
页码:
19-23
栏目:
试验与研究
出版日期:
2018-04-28

文章信息/Info

Title:
Study on Microstructure and Properties of Alloy Pipe with
Inner Wall Quench Hardening
文章编号:
10.19291/j.cnki.1001-3938.2018.04.004
作者:
黄晓辉1;  2; 李华彬3; 牛爱军1;  2; 秦廷许3
1. 国家石油天然气管材工程技术研究中心，陕西 宝鸡 721008；
2. 宝鸡石油钢管有限责任公司，陕西 宝鸡 721008；
3. 四川龙蟒矿冶有限责任公司，四川 攀枝花 617112
Author(s):
HUANG Xiaohui1.2;   LI Huabin3;   NIU Aijun1.2;   QIN Tingxu3
1. Chinese National Engineering Technology Research Center for Petroleum and Natural Gas Tubular Goods, Baoji 721008, Shaanxi, China;
2. Baoji Petroleum Steel Pipe Co., Ltd., Baoji 721008, Shaanxi, China; 3. Sichuan Lomon Mining and Metallurgical Co., Ltd., Panzhihua 617112, Sichuan, China
关键词:
淬火; 内壁硬化; 合金管; 马氏体; 组织均匀
Keywords:
quenching;  inner wall hardening;  alloy pipe;  martensite;  structure homogeneity
分类号:
TG113
DOI:
10.19291/j.cnki.1001-3938.2018.04.004
文献标志码:
A
摘要:
为了对内壁淬火硬化合金管组织性能进行研究，采用化学分析、金相试验、硬度试验、冲击试验以及拉伸试验等方法，分别对合金管成分、力学性能及其金相组织等方面进行了检验和分析。试验结果显示：内壁硬化合金管化学成分主要为C、Si、Mn元素；经过内壁淬火后，直管和弯管试样内层组织均为马氏体，直管淬火层平均深度约为5.9 mm，弯管约为7.9 mm；直管淬火层平均洛氏硬度HRC50，弯管淬火层平均洛氏硬度HRC40；直管和弯管内表面层经过淬火后组织不均匀。分析结果表明，内壁淬火硬化合金管具备一定的耐磨损性，可以作为输矿用耐磨管并安全服役；直管和弯管内表面层经过淬火后组织不均匀，后期可改进淬火工艺，使组织均匀进而真实反映管材强度。
Abstract:
In order to study the microstructure and properties of alloy pipe with inner wall quench harding, using mechanical properties, chemical analysis, hardness test, impact test and tensile test, the composition, mechanical properties and microstructure were tested and analyzed. The results show that the chemical constituents of the alloy pipe with inner wall hardening are mainly C, Si, Mn elements. After quenching the inner wall of alloy pipe, the inner layer microstructure of specimens of straight pipe and bending pipe is martensite, but the surface layer microstructure  is inhomogeneity. The average depth of straight pipe quenching layer is about 5.9 mm, the average depth of bending pipe quenching layer is about 7.9 mm, the average Rockwell hardness number of straight pipe quenching layer is HRC50, and the average Rockwell hardness number of bending pipe quenching layer is HRC40. The analysis results show that the alloy pipe with inner wall quenches hardening has certain abrasion resistance, which can be used as wear-resistant pipe for ore-conveying and is safe to serve; the surface layer microstructure of straight pipe and bending pipe is not uniform after quenching, and the quenching process can be improved later, so that the microstructure is homogeneous and the then truly reflect the strength of the pipe.

参考文献/References:

[1] 钱桂华， 曹晰. 浆体管道输送设备实用选型手册[M]. 北京： 冶金工业出版社， 1995.
[2] 邹伟生， 袁海燕， 罗绍卓. 长距离管道输送发展现状及在矿山的应用前景[J]. 金属材料与冶金工程， 2009， 37（1）： 57-60.
[3] 温新林， 唐贵基， 贾建民，等. 中国电力行业耐磨管道技术及标准的研究与工作进展状况[J]. 热处理技术与装备， 2012， 33（3）： 58-62.
[4] 董刚. 材料冲蚀行为及机理研究[D]. 杭州： 浙江工业大学， 2004.
[5] 唐川林， 张晓琪， 张凤华，等.  用于疏浚江河湖泊的新型高效工具研究[J].  湖南工业大学学报， 2002， 16（4）：  105-108.
[6] 吴湘福. 矿浆管道输送技术的发展与展望[J]. 金属矿山，2000（6）： 17.
[7] 韩文亮. 浆体管道输送的发展及输送的工艺设计[J]. 金属矿山， 2006（S1）： 85-88.
[8] 瓦斯普. 固体物料的浆体管道输送[M]. 北京： 水利电力出版社， 1980.
[9] 许辉， 幺克威， 张兴兵，等. 一种钢管内壁硬化淬火设备及淬火方法： 中国， CN103305678[P]. 2013-09-18.
[10] 许辉， 幺克威， 张兴兵， 等. 一种弯钢管内壁硬化淬火设备： 中国， CN203360495[P]. 2013-12-25.
[11] 张继军，桂晓莉. 浆体管道磨损机理研究[J]. 甘肃科技， 2011， 27（1）： 60-63.
[12] 康进兴， 赵文轮，朱金华. 材料抗冲蚀性的研究进展[J]. 材料保护， 2001， 34（10）： 22-23.

相似文献/References:

[1]魏志涛,王　燕,马　骏.HFW焊管焊缝热处理水淬布局及空冷长度的选择[J].焊管,2011,34(6):36.[doi:１００１－3938(2011)06-0036-03]
　WEI Zhi-tao,WANG Yan,MA Jun.Water Quenching Layout and Selecting Air-cooling Length for HFW Pipe Weld Heat Treatment[J].,2011,34(4):36.[doi:１００１－3938(2011)06-0036-03]
[2]刘振双.GCr15钢焊管轧辊的热处理工艺[J].焊管,2012,35(2):37.[doi:１００１－３９３８（２０１２）０２-0037-04]
　LIU Zhen-shuang.Heat Treatment Process of Welded Pipe Roller Made by GCr15 Steel[J].,2012,35(4):37.[doi:１００１－３９３８（２０１２）０２-0037-04]

备注/Memo

备注/Memo:

收稿日期：2017-12-15

基金项目： 国家863项目课题“双金属层状复合管材技术研究”（项目编号2013AA031303）。
作者简介：黄晓辉（1980—），男，高级工程师，硕士，主要从事油气输送管材的开发工作。

更新日期/Last Update: 2018-05-28