[1]何石磊,等.一种稠油热采井用抗硫套管试验研究[J].焊管,2018,41(11):6-11.[doi:10.19291/j.cnki.1001-3938.2018.11.002]
　HE Shilei,LIANG Hang,et al.Study on a H2S Stress Corrosion Resistance Casing for Heavy Oil Thermal Recovery Wells[J].,2018,41(11):6-11.[doi:10.19291/j.cnki.1001-3938.2018.11.002]
点击复制

一种稠油热采井用抗硫套管试验研究()
分享到：

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
41
期数:
2018年第11期
页码:
6-11
栏目:
试验与研究
出版日期:
2018-11-28

文章信息/Info

Title:
Study on a H2S Stress Corrosion Resistance Casing
for Heavy Oil Thermal Recovery Wells
文章编号:
10.19291/j.cnki.1001-3938.2018.11.002
作者:
何石磊1;  2; 梁 航1;  2; 王 涛1;  2; 李远征1;  2; 任永峰1;  2; 黄晓江1;  2;  杨 军2; 焦 斌2
1. 国家石油天然气管材工程技术研究中心，陕西 宝鸡 721008；
2. 宝鸡石油钢管有限责任公司，陕西 宝鸡 721008
Author(s):
HE Shilei1;  2;  LIANG Hang1;  2;  WANG Tao1;  2;  LI Yuanzheng1;  2;  REN Yongfeng1;  2; HUANG Xiaojiang1; 2;  YANG Jun2;  JIAO Bin2
1. Chinese National Engineering Technology Research Center for Petroleum and Natural Gas Tubular Goods , Baoji 721008, Shannxi, China；
 2. Baoji Petroleum Steel Pipe Co., Ltd., Baoji 721008, Shannxi, China
关键词:
抗硫套管; 高温强度; 线膨胀系数; 应力腐蚀
Keywords:
sulfate resistant casing;  high temperature strength;  linear expansion coefficient;  stress corrosion
分类号:
TG115.5
DOI:
10.19291/j.cnki.1001-3938.2018.11.002
文献标志码:
A
摘要:
为了保证稠油热采井工况下石油套管的性能，采用低碳Cr-Mo钢和V、Ti等元素微合金化的设计，利用纯净钢冶炼技术，并配合适当的“高频电阻焊+热张力减径+热处理工艺”的生产工艺，设计出了一种稠油热采井用抗硫套管。对试制套管的几何尺寸、力学性能、高温性能、腐蚀性能等进行了检测分析。结果表明：试制套管的几何尺寸精度高，椭圆度≤0.25%，壁厚不均度≤6%；强韧性匹配好，具有较高的高温强度和低的线膨胀率，在350 ℃高温时屈服强度折损率≤15%，拉伸强度折损率≤10%，线膨胀率≤15%；抗硫化氢应力腐蚀性能优异，依据NACE TM 0177标准中A法A溶液，在加载496 MPa应力下H2S应力腐蚀720 h后试样不开裂；同时，还具有优异的抗外压挤毁和内压至失效性能。
Abstract:
In order to ensure the performance of casing in heavy oil thermal recovery wells, a new kind of casing product with sulfur stress corrosion resistance for heavy oil thermal recovery wells was developed by using low carbon Cr-Mo steel-based chemical composition, micro-alloying with addition of V and Ti, adoption of clean-steel metallurgical technology and appropriate production process on the basis of high frequency electrical resistance welding and forming-hot stretch reducing-heat treatment technology. The performances were tested and analyzed such as geometry dimension, mechanical properties, high temperature performance, linear expansion coefficient and sulfide stress corrosion cracking and so on. The results show that the geometric size of the trial casing product is accurate, less than 0.25% in ovality and less than 6% in eccentricity. The casing has high strength and toughness, good high temperature strength and low linear expansion rate. At 350 ℃, the yield strength loss rate is less than 15%, the tensile strength loss rate is not more than 10%, the linear expansion rate is lower than 15%. Excellent， hydrogen sulfide stress corrosion resistance was proved by experiment that the specimen loaded about 496 MPa stress by using a method has no crack after 720 h in a solution according to NACE TM 0177 standard. And it has also excellent practical properties of some full-length casing like bursting and collapse.

参考文献/References:

[1] 马利娟. 杨楼油田稠油热采井套损原因分析及预防措施[J]. 河南化工，2016，33（5）：48-51.
[2] 赵旭亮. 稠油热采井套损防治措施及计算理论[J]. 石油地质与工程，2012，26（4）：122-124.
[3] 甘全. 热采井套管损坏机理研究[D]. 成都：西南石油大学，2017.
[4] 秦滔. 欢西油田热采井套损机理及影响因素分析[D]. 大庆：东北石油大学，2015.
[5] 林日亿，宋多培，周广响，等. 热采过程中硫化氢成因机制[J]. 石油学报，2014，35（6）：1153-1159.
[6] 林日亿，罗建军，王新伟，等. 非含硫金属盐对稠油水热裂解生成硫化氢影响实验[J]. 石油学报，2016，37（2）：237-241.
[7] 宫俊峰，王秋霞，刘岩. 不同形态硫化物对稠油热采硫化氢产生的贡献分析[J]. 油气地质与采收率，2015，22（4）：93-96.
[8] 扈立，赵强，李恒政，等. 火驱稠油热采井TP90H-9Cr套管热处理工艺优化试验研究[J]. 钢管，2016，45（5）：9-14.
[9] 卢小庆，扈立，李恒政，等. 火烧油层稠油热采井专用套管的设计开发[J]. 钢管，2013，42（3）：39-43.
[10] 周丹，黄云，黄英，等. 一种经济型稠油热采专用套管的研发[J]. 四川冶金，2016，38（3）：29-34.
[11] 张行刚，石晓霞，刘金，等. 稀土微合金化稠油热采井套管BT100H的研究[J]. 石油管材与仪器，2018，4（1）：50-54.
[12] 田琨，王正，扈立，等. 超深复杂井用非标准规格TP140V套管的开发[J]. 钢管，2018，47（1）：13-17.
[13] 杨雪春. 热处理对稠油热采井专用套管HS110H的组织和性能的影响[J]. 齐齐哈尔大学学报（自然科学版），2014，30（2）：72-76.
[14] 何石磊，张峰，毕宗岳，等. C90级耐腐蚀HFW套管性能试验研究[J]. 焊管，2014，37（8）：5-11.
[15] 周志伟，俞杰. C90-1级耐腐蚀石油套管用钢25CrMoTi的开发[J]. 特殊钢，2012，33（4）：39-41.
[16] 余灿生. C95级ERW耐腐蚀油井管成分及热处理工艺研究[D]. 昆明：昆明理工大学，2013.
[17] 操龙飞，徐光，邓鹏，等. 低合金钢热膨胀系数测定和分析[J]. 材料科学与工艺，2013，21（3）：105-109.
[18] 娄琦，杜伟，李东风，等. 110钢级抗挤抗硫套管性能试验研究[J]. 石油矿场机械，2013，42（5）：65-68.
[19] 孙宇，张志远，韩丽华，等. 铬钼系列抗腐蚀钢管的组织及析出相分析[J]. 钢管，2011，40（6）：43-48.
[20] 娄琦，杜伟，李东风，等. 抗硫套管的成分与性能分析[J]. 管道技术与设备，2013（5）：7-9.

备注/Memo

备注/Memo:
 收稿日期：2018-08-20
作者简介：何石磊（1983—），男，硕士，主要从事油井管工艺研究和新产品开发工作。
更新日期/Last Update: 2019-01-14