[1]田永吉,李阳才,屈绪良,等.J55钢级SEW管坯焊缝压扁开裂问题研究[J].焊管,2018,41(12):48-55.[doi:10.19291/j.cnki.1001-3938.2018.12.011]
　TIAN Yongji,LI Yangcai,QU Xuliang,et al.Study on the Weld Cracking Problem of Flattening the SEW J55 Tube Blank[J].,2018,41(12):48-55.[doi:10.19291/j.cnki.1001-3938.2018.12.011]
点击复制

J55钢级SEW管坯焊缝压扁开裂问题研究()
分享到：

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
41
期数:
2018年第12期
页码:
48-55
栏目:
经验交流
出版日期:
2018-12-28

文章信息/Info

Title:
Study on the Weld Cracking Problem of Flattening the SEW J55 Tube Blank
文章编号:
10.19291/j.cnki.1001-3938.2018.12.011
作者:
田永吉; 李阳才; 屈绪良; 苏 琬
宝鸡石油钢管有限责任公司，陕西 宝鸡 721008
Author(s):
TIAN Yongji; LI Yangcai; QU Xuliang; SU Wan
关键词:
压扁开裂; J55钢级; SEW套管; 喷水控冷; 化学成分
Keywords:
flattening crack; J55 steel grade; SEW casing; water spray control; chemical composition
分类号:
TG335.75
DOI:
10.19291/j.cnki.1001-3938.2018.12.011
文献标志码:
B
摘要:
为了解决J55钢级SEW管坯生产中焊缝压扁开裂问题，对压扁开裂的原因进行了分析，同时针对性的对喷水控冷工艺进行了研究，对管坯卷板化学成分进行了改进并批量试制。分析表明，管端出现回火马氏体和微量贝氏体等脆性组织是造成SEW J55管坯焊缝压扁开裂的直接原因。研究结果显示，在管坯控冷前增加风冷环以减少管坯西端内壁进水量、降低管坯入水冷环前的温度和控冷水量，可改善管坯的压扁性能。批量试制结果说明，Ti元素是SEW J55管坯控冷工艺生产中管坯压扁开裂的主要影响因素；在卷板生产时增加Nb含量、控制并降低Ti的含量，能够解决管坯控冷后压扁开裂问题。
Abstract:
In order to solve the problem of weld cracking in SEW J55 tube blank production， the causes of flattening cracking was analyzed. At the same time，the control technology of water-cooling was studied in detail， and batch trial production after the chemical composition of the tube blank was improved. The analysis shows that the brittle structure such as tempered martensite and micro-bainite at the end of the pipe is the direct cause of the flattening cracking of the SEW J55 tube blank weld. The results show that the air-cooling ring can be added before the tube blank is controlled to reduce the water inflow at the inner end of the tube blank， reduce the temperature before the tube blank enters the water-cooling ring， and control the amount of cold water, which can improve the flattening performance of the tube blank. The results of batch trial production show that Ti element is the main influencing factor of tube blank cracking in SEW J55 tube blank controlled cooling process production.

参考文献/References:

[1] API SPEC 5CT—2011，套管和油管规范[S].
[2] 胡光立，谢希文. 钢的热处理[M]. 西安：西北工业大学出版社，2004.
[3] 赵振东. 新钢种热处理工艺设计[J]. 新技术新工艺，1992（2）：6－10.
[4] 徐恒钧. 材料科学基础[M]. 北京：北京工业大学出版社，2001.
[5] 太和久重雄. 热处理108法[M]. 北京：机械工业出版社，1986.
[6] 刘国勋. 金属学原理[M]. 北京：冶金工业出版社，1979.
[7] 戚正风. 金属热处理原理[M]. 北京：机械工业出版社，1981.
[8] 戚正风. 固态金属中的扩散与相变[M]. 北京：机械工业出版社，1998.
[9] 曾正明. 实用钢铁材料手册[M]. 北京：机械工业出版社，2015.
[10] 李国彬. 热处理工艺规范与数据手册[M]. 北京：化学工业出版社，2013.

备注/Memo

备注/Memo:

收稿日期：2018－09－06

作者简介：田永吉（1984—），工程师，主要从事SEW油套管工艺、质量管理工作。

更新日期/Last Update: 2019-01-15