[1]李晓亮,韩 亮.非标高压容器厚壁不锈钢复合钢板焊接工艺评定[J].焊管,2021,44(8):12-17.[doi:10.19291/j.cnki.1001-3938.2021.08.004]
　LI Xiaoliang,HAN Liang.Welding Procedure Qualification of High Pressure Thick Wall Composite Steel Plate for Non-standard Vessels[J].,2021,44(8):12-17.[doi:10.19291/j.cnki.1001-3938.2021.08.004]
点击复制

非标高压容器厚壁不锈钢复合钢板焊接工艺评定()
分享到：

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
第44卷
期数:
2021年第8期
页码:
12-17
栏目:
应用与开发
出版日期:
2021-08-28

文章信息/Info

Title:
Welding Procedure Qualification of High Pressure Thick Wall Composite Steel Plate for Non-standard Vessels
文章编号:
10.19291/j.cnki.1001-3938.2021.08.004
作者:
李晓亮; 韩 亮
四川石油天然气建设工程有限责任公司，成都 610051
Author(s):
LI Xiaoliang;  HAN Liang
Sichuan Petroleum and Natural Gas Construction Engineering Co., Ltd., Chengdu 610051, China
关键词:
非标容器; 不锈钢厚壁复合板; 焊接工艺; 工艺评定
Keywords:
non-standard containers;  stainless steel thick-wall composite plate;  welding technology;  procedure qualification
分类号:
TG441
DOI:
10.19291/j.cnki.1001-3938.2021.08.004
文献标志码:
B
摘要:
以土库曼斯坦南约洛坦气田的非标容器在焊接中遇到的问题为工程背景，对非标容器涉及到的（138+3）mm厚壁Q345R（R-HIC）+022Cr17Ni12Mo2不锈钢复合板进行了焊接工艺评定试验。通过增加复层倾角，并按照基层、过渡层、复层的顺序逐次完成焊接，焊后对厚壁复合板焊接工艺进行评定，同时分别测定了试样的力学性能、基层焊缝HIC性能、复层焊缝耐蚀性等。结果表明，采用此种工艺焊接的厚壁钢板具有良好的力学性能，基层焊缝抗HIC评价合格，复层焊缝具有较强的耐蚀性，均符合国标要求。此次评定试验为土库曼斯坦南约洛坦气田6台吸收塔焊接提供了技术保障。
Abstract:
Based on the engineering background of the problems encountered in the welding of non-standard vessels in South Yolotan gas field in Turkmenistan, the welding procedure qualification test of(138+3) mm wall thickness Q345R(R-HIC)+022Cr17Ni12Mo2 stainless steel thick-walled composite plates involved in the non-standard vessels is carried out. By increasing the Angle of cladding layer and completing the welding successively to the order of base layer, transition layer and cladding layer. After welding, the welding process of thick-wall composite plate was tested and evaluated. The mechanical properties of the sample, the HIC properties of the base weld and the corrosion resistance of the cladding weld were measured respectively. The results show that the thick-wall steel plate welded by this process has good mechanical properties, the HIC evaluation of the base weld is qualified, and the corrosion resistance of the cladding weld is good, all of which meet the requirements of the national standard. This evaluation test provides technical support for the welding of 6 absorbers in South Yolotan gas field of Turkmenistan.

参考文献/References:

[1] 林桂贤，李义民，朵元才，等. Q345R+12Cr2Mo1R异种钢焊接及热处理试验研究[J]. 压力容器，2020，37（6）：15-18.

[2] 周海涛，徐连玉，赵振亮，等. 核电站大径厚壁不锈钢管道焊接技术探究[J]. 电力工程，2020（6）：148-150.
[3] 朵元才，张伟，靳海军，等. 焊后热处理时间对12Cr2Mo1R钢埋弧焊焊接接头组织和力学性能的影响[J]. 中国化工装备，2018，20（6）：43-46.
[4] 赵蕾. Q345R压力容器板性能分析与研究[J]. 物理测试，2012（1）：5-7，16.
[5] 严春妍，李午申，薛振奎，等. LNG储罐用9%Ni钢及其焊接性[J]. 焊接学报，2008（6）：49-52.
[6] 黄静，赵国仙，宋洋. Q345R钢埋弧焊焊缝开裂原因分析[J]. 焊管，2020，43（3）：56-62.
[7] DAI H L，SHI S W，GUO C，et al. Pits formation and stress corrosion cracking behavior of Q345R in hydrofluoric acid[J]. Corrosion Science，2020，15（166）：1-12.
[8] DING W J，SHI H，XIU Y L，et al. Hot corrosion behavior of commercial alloys in thermal energy storage material of molten MgCl2/KCl/NaCl under inert atmosphere[J]. Solar Energy Materials and Solar Cells，2018（184）：22-30.
[9] 王庆伟. 重型压力容器裙座与设备本体同炉焊后热处理技术[J]. 中国重型装备，2017（2）：44-47.
[10] 段莉蕾，李志杰，高永光，等. 奥氏体不锈钢焊条焊缝金属低温韧性试验[J]. 压力容器，2020（11）：8-14.
[11] 王洋，魏耀华，郑青昊，等. X80大壁厚螺旋埋弧焊管外焊坡口角度研究[J]. 焊管，2014（7）：63-67.
[12] 原国栋. 不锈钢复合钢板焊接接头中过渡层的焊接问题[J]. 热加工工艺，2007（7）：89-90.

备注/Memo

备注/Memo:
收稿日期：2021-06-16
作者简介：李晓亮（1986—），男，陕西富平人，本科毕业于西安石油大学材料成型及控制工程专业，工程师，主要从事压力容器及油气田工程建设工作。
更新日期/Last Update: 2021-08-27