[1]马锋,范冬艳,刘凤兰.注气井油管钢应力腐蚀的实验室评价方法优化[J].焊管,2023,46(8):25-29.[doi:10.19291/j.cnki.1001-3938.2023.08.004]
　MA Feng,FAN Dongyan,LIU Fenglan.Optimization of Laboratory Evaluation Method for Stress Corrosion of Tubing Steel in Gas Injection Wells[J].,2023,46(8):25-29.[doi:10.19291/j.cnki.1001-3938.2023.08.004]
点击复制

注气井油管钢应力腐蚀的实验室评价方法优化()
分享到：

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
46
期数:
2023年第8期
页码:
25-29
栏目:
试验与研究
出版日期:
2023-08-19

文章信息/Info

Title:
Optimization of Laboratory Evaluation Method for Stress Corrosion of Tubing Steel in Gas Injection Wells
文章编号:
10.19291/j.cnki.1001-3938.2023.08.004
作者:
马锋; 范冬艳; 刘凤兰
1.中国石油天然气股份有限公司吉林油田分公司， 吉林 松原 138000；
2.二氧化碳驱油与埋存试验基地， 吉林 松原 138000
Author(s):
MA Feng; FAN Dongyan; LIU Fenglan
1. PetroChina Jilin Oilfield Company, Songyuan 138000, Jilin, China;
2. Carbon Dioxide Flooding and Storage Test Base, Songyuan 138000, Jilin, China
关键词:
CO2驱油; 油管失效; 应力腐蚀; 三点弯; 环空保护液
Keywords:
CO2 flooding;  tubing failure;  stress corrosion;  three?oint bending;  annular protection fluid
分类号:
TG113.231
DOI:
10.19291/j.cnki.1001-3938.2023.08.004
文献标志码:
A
摘要:
CO2腐蚀是制约CO2驱油与埋存注入井筒安全平稳生产的关键问题，由于注入介质与服役环境的特殊性，导致CO2注入井油管因应力腐蚀而失效，大量研究认为，吉林油田CO2驱注气井环境的低温、CO2、细菌及H2S等因素是造成油管硫化物应力腐蚀的主要原因，因此寻找一种适合注气井酸性高压服役环境应力腐蚀的评价方法尤为重要。采用不同试验温度、腐蚀溶液、H2S制备方法和加载方式等试验方法，对油管钢应力腐蚀及腐蚀形貌进行分析测定，建立了适用于吉林油田CO2驱注气井环境的油管钢应力腐蚀分析技术及评价方法。通过油基环空保护液应用，阻断了应力腐蚀敏感环境，提高了注入管柱的应力腐蚀防护性能，矿场试验防治效果良好。
Abstract:
CO2 corrosion is the key problem that restricts the safe and stable production of CO2 flooding and storage injection wellbore. Due to the particularities of injection medium and service environment, the tubing of CO2 injection well is fractured.A large number of studies have suggested that low temperature, CO2, bacteria and H2S in CO2 injection wells in Jilin oilfield are the main causes of sulfide stress corrosion. Therefore, it is particularly important to find an evaluation method suitable for stress corrosion in acid high?ressure service environment of gas injection wells.Through the determination of test temperature, corrosion solution, preparation method of H2S and loading mode, and the analysis and determination of stress corrosion and corrosion morphology of tubing steel by different experimental methods, the stress corrosion analysis technology and evaluation method of tubing steel for CO2 injection well environment in Jilin oilfield were established. The application of oil?ased annular protection fluid can block the stress corrosion sensitive environment and improve the stress corrosion protection performance of the injection string. Field tests show that the control effect is good, and stress corrosion almost does not occur in this environment.

参考文献/References:

[1]张星， 李兆敏， 马新忠，等.深井油管H2S应力腐蚀实验研究[J].石油勘探与开发，2004， 31（6）：95-97.[2]张清， 李全安， 文九巴，等.CO2/H2S对油气管材的腐蚀规律及研究进展[J].腐蚀与防护， 2003，24（7）：227-281.[3]赵明纯，单以银，李玉海，等.显微组织对管线钢硫化物应力腐蚀开裂的影响[J].金属学报， 2001，37（10）：1087-1092.[4]美国腐蚀工程师协会，油田设备用抗硫化物应力开裂金属材料：NACE MR–01–75[S].休斯敦：NACE，1975.[5]吕建华，关小军，徐洪庆，等.影响低合金钢材抗H2S腐蚀的因素[J].腐蚀科学与防护技术，2006，18（2）：118-121.[6]IGI S.中国西气东输二线管道延性断裂分析（一）[J].焊管，2008，31（2）：23-26.[7]村田正彦.日本新日铁X80级管线钢管研究概述[J].焊管，2008，31（2）：40-43，94.[8]IGI S.中国西气东输二线管道延性断裂分析（二）[J].焊管，2008，31（3）：33-38.[9]蔡彬，郑福恩，李记科，等.海底油气管道延性断裂止裂CVN冲击功的计算[J].焊管，2011，34（12）：39-42.[10]陈小伟，王旭，郭立萍，等.抗延性断裂X80厚壁直缝埋弧焊管的研发[J].焊管，2018，41（9）：6-14.[11]崔富凯，甄莹.高钢级管道延性断裂过程中壁厚减薄率研究[J].焊管，2021，44（10）：1-6，12.[12]郭崇晓，蒋钦荣，张燕飞，等.双金属复合管内覆（衬）层应力腐蚀开裂失效原因分析[J].焊管，2016，39（2）：33-38.

备注/Memo

备注/Memo:
收稿日期：2022-10-11
基金项目：中国石油集团公司重大科技专项课题“CCUS 注采工艺、产出气循环利用及高效防腐关键技术研究”（项目编号2021ZZ01-04）；中国石油集团公司重大科技专项课题“松辽盆地（大庆、吉林）CCUS 技术集成与工业化试验”（项目编号2021ZZ01-08）。
作者简介：马锋（1982—），男，高级工程师，大学本科，2005年毕业于西南石油大学应用化学专业，现就职于吉林油田油气工程研究院CO2驱油与埋存工程实验室，主要从事CO2驱腐蚀防护技术研究工作。