[1]马立立,李雅可,郭锦龙,等.快速冷处理对高强度管线钢X120热影响区的微观组织和韧性的影响[J].焊管,2013,36(6):68-72.[doi:1001-3938(2013)06-0068-05]
 Edited and Translated by MA Lili,LI Yake,GUO Jinlong,et al.Effect of fast cooling process on the microstructure and toughness of heat-affected zone in a high strength pipeline steel X120[J].,2013,36(6):68-72.[doi:1001-3938(2013)06-0068-05]
点击复制

快速冷处理对高强度管线钢X120热影响区的微观组织和韧性的影响
分享到:

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
36
期数:
2013年第6期
页码:
68-72
栏目:
国外焊管
出版日期:
2013-06-28

文章信息/Info

Title:
Effect of fast cooling process on the microstructure and toughness of heat-affected zone in a high strength pipeline steel X120
文章编号:
1001-3938(2013)06-0068-05
作者:
马立立李雅可郭锦龙王 涛钱 勇 编译
(渤海装备南京巨龙钢管有限公司,南京 210061)
Author(s):
Edited and Translated by MA Lili LI Yake GUO Jinlong WANG Tao QIAN Yong
(Bohai Equipment Nanjing Julong Steel Pipe Co., Ltd., Nanjing 210061, China)
关键词:
管线钢快速冷却热影响区微观组织冲击韧性
Keywords:
pipeline steel fast cooling process heat-affected zone microstructure impact toughness
分类号:
TG142.1
DOI:
1001-3938(2013)06-0068-05
文献标志码:
A
摘要:
焊接过程中通过快速冷却减少Ac3温度以上的高温保持时间和从800 ℃降到500 ℃的冷却时间,从而改善焊接热影响区的韧性。并通过光学显微镜和扫描电子观察不同热循环作用的热影响区的微观组织发现,缩短高温保持时间可使热影响区变窄,熔合线奥氏体晶粒变细和热影响区晶粒变粗大;然而,缩短从800 ℃到500 ℃的冷却时间可使热影响区贝氏体铁素体晶粒细化。熔合线M/A组分在数量和尺寸上有所减小,并且大部分转变成长条状。试验结果表明,快速冷却处理在改善X120管线钢热影响区韧性方面起着重要的作用。
Abstract:
A process for improving the heat-affected zone toughness by fast cooling during welding was developed. The holding time at high temperature above Ac3 and the cooling time from 800 ℃ to 500 ℃ were decreased when welding thermal cycle was experienced by fast cooling process. The microstructures in the heat-affected zone with varied thermal cycles were examined by optical and scanning electron microscopes. The shorten holding time led to thinner heat-affected zone width and finer austenite grains in the fusion line and coarse-grained heat-affected zone; while the decreased cooling time from 800 ℃ to 500 ℃ resulted in finer bainitic ferrite in the heat-affected zone. Martensite-austenite constituents in the fusion line were reduced in amount and size and predominantly changed into film-like in shape. Experimental results indicated that the fast cooling process played an important role in improving the heat-affected zone toughness of pipeline steel X120.

参考文献/References:

[1] KNEISSL A C, GARCIA C I, DEARDO A J.In HSLA Steels, Processing, Properties and Applications[M].Warrendale:The Minerals, Metals & Materials Society,1992:99-105.
[2] GLADMAN T.The Physical Metallurgy of Microalloyed Steels[M].London: The Institute of Materials,1997.
[3] SHIKANAI N,MITAO S,ENDO S.Recent Development in microstructural Control Technologies Through the Thermo-mechanical Control Process(TMCP) with JFE Steel’s High-performance Plates, JFE Technical Report11[M].Tokyo: JFE Steel Corporation,2008.
[4] SONG W H, SEO D H,YOO J Y.Mechanical Properties and Microstructure of X100 Grade Pipe Welds[C]//Conference on Pipeline Technology.Ostend:[s.n.],2009:24-30.
[5] SHOME M,GUPTA O P,MOHANTY O N.A Modified Analytical Approach for Modeling Grain Growth in the Coarse Grain HAZ of HSLA Steels[J]. Scripta Mater, 2004(50):1007-1010.
[6] HULKA K.Modern Processing Facilities Favour the Application of Microalloyed Steels[C]//Proceeding International Conference on clean steel.Balatonszeplak:[s.n.],1992:4-8.
[7] ASHBY M F,EASTERLING K E.A First Report on Diagrams for Grain Growth in Welds[J]. Acta Metall,198230(11):1969-1978.
—————————

相似文献/References:

[1]李新华,罗金恒,赵新伟,等.高钢级管线钢失效评估曲线研究[J].焊管,2007,30(4):33.[doi:1001-3938(2007)04-0033-03]
 LI Xin-hua,LUO Jin-heng,ZHAO Xin-wei,et al.Research on Failure Assessment Curves of High Grade Pipeline Steel[J].,2007,30(6):33.[doi:1001-3938(2007)04-0033-03]
[2]宫少涛,王爱民,吉玲康,等.X80与X100级管线钢屈服强度Rt 0.5与Rp 0.2的差异性研究[J].焊管,2007,30(5):42.[doi:1001-3938(2007)05-0042-03]
 GONG Shao-tao,WANG Ai-min,JI Ling-kang,et al.Study on Difference Between Yield Strength Rt 0.5 and Rp 0.2 for X80 and X100 Pipelines Steel[J].,2007,30(6):42.[doi:1001-3938(2007)05-0042-03]
[3]刘庆才,李 东,黎剑锋.影响输气管线钢管抗H2S性能主要因素的探讨[J].焊管,2007,30(5):54.[doi:1001-3938(2007)05-0054-05]
 LIU Qing-cai,LI Dong,LI Jian-feng.Key Factors Affecting Sour Service Ability of Welded Pipe and Its Domestic Production[J].,2007,30(6):54.[doi:1001-3938(2007)05-0054-05]
[4]王树人,崔志新.管线钢落锤撕裂试验异常脆性断口分析[J].焊管,2007,30(6):69.[doi:1001-3938(2007)06-0069-03]
 WANG Shu-ren? CUI Zhi-xin.Analysis on Abnormal Brittle Fracture of DWTT for Pipeline Steel[J].,2007,30(6):69.[doi:1001-3938(2007)06-0069-03]
[5]陶 鹏,张 弛,杨志刚,等.高钢级管线钢的组织和力学性能[J].焊管,2008,31(2):19.[doi:1001-3938(2008)02-0019-04]
 TAO Peng,ZHANG Chi,YANG Zhi-gang,et al.The Microstructure and Mechanical Property of X70,X80 and X100 Grade Pipeline Steel[J].,2008,31(6):19.[doi:1001-3938(2008)02-0019-04]
[6]黄明浩,徐 烽,黄国建.影响管线钢屈强比的因素探讨[J].焊管,2008,31(3):20.[doi:1001-3938(2008)03-0020-04]
 HUANG Ming-hao,XU Feng,HUANG Guo-jian.Discussion on Influencing Factors of Yield Ratio for Pipeline Steel[J].,2008,31(6):20.[doi:1001-3938(2008)03-0020-04]
[7]牛 辉,余大涛,高惠临.管线钢焊接热影响区的组织预测[J].焊管,2008,31(3):28.[doi:1001-3938(2008)03-0028-05]
 NU Hui,YU Da-tao,GAO Hui-lin.Structure Forecast of Pipeline Steel Welding Heat Affected Zone[J].,2008,31(6):28.[doi:1001-3938(2008)03-0028-05]
[8]孔君华,郑 琳,关 云,等.西气东输二线工程用18.4 mm厚 X80级热轧板卷生产实践[J].焊管,2008,31(6):50.[doi:1001-3938(2008)06-0050-04]
 KONG Jun-hua,ZHENG Ling,GUAN Yun,et al.Production Experience of X80 Grade Hot Rolled Coil with 18.4 mm Thickness Used〖JZ〗for the Second West to East Gas Pipeline Project[J].,2008,31(6):50.[doi:1001-3938(2008)06-0050-04]
[9]黄国建,张英慧,孔祥磊,等.特厚规格X70和X80级热轧卷板的开发与应用[J].焊管,2009,32(2):17.[doi:1001-3938(2009)02-0017-06]
 HUANG Guo-jian,ZHANG Ying-hui,KONG Xiang-lei,et al.Development and Application of X70 & X80 Grade HRC with Heavy Thickness[J].,2009,32(6):17.[doi:1001-3938(2009)02-0017-06]
[10]杨专钊,李云龙,邓波,等.管线钢拉伸试验中异常屈服强度研究与分析[J].焊管,2009,32(4):51.[doi:1001-3938(2009)04-0051-03]
 YANG Zhuan-zhao,LI Yun-long,DENG Bo,et al.Research and Analysis of Abnormal Yield Strength during Tensile Test of Pipeline Steel[J].,2009,32(6):51.[doi:1001-3938(2009)04-0051-03]

备注/Memo

备注/Memo:
译者简介:马立立(1984—),女,助理工程师,主要从事直缝埋弧焊钢管产品质量管理工作。
更新日期/Last Update: