[1]张俊宝,唐 识,梅 乐,等.埋弧堆焊低合金钢熔敷金属组织和性能研究[J].焊管,2016,39(8):16-18,22.[doi:10.19291/j.cnki.1001-3938.2016.08.004]
　ZHANG Junbao,TANG Shi,MEI Le,et al.Study on Microstructure & Properties of Submerged Arc Surfacing Welding Low-alloy Steel Weld Metal[J].,2016,39(8):16-18,22.[doi:10.19291/j.cnki.1001-3938.2016.08.004]
点击复制

埋弧堆焊低合金钢熔敷金属组织和性能研究
分享到：

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
39
期数:
2016年第8期
页码:
16-18,22
栏目:
试验与研究
出版日期:
2016-08-28

文章信息/Info

Title:
Study on Microstructure & Properties of
Submerged Arc Surfacing Welding Low-alloy Steel Weld Metal
文章编号:
10.19291/j.cnki.1001-3938.2016.08.004
作者:
张俊宝1; 唐 识2; 梅 乐1; 余 燕1
1. 上海核工程研究设计院， 上海 200233；
2. 国核示范电站有限责任公司， 山东 荣成 264312
Author(s):
ZHANG Junbao1;  TANG Shi2;  MEI Le1;  YU Yan1
1. Shanghai Nuclear Engineering Research & Design Institute, Shanghai 200233, China;
2. State Nuclear Power Demonstration Plant Co., Ltd., Rongcheng 264312, Shandong, China
关键词:
CAP1000; 堆测接管管座; 埋弧焊; 堆焊
Keywords:
CAP1000;  pressure vessel tube socket;  submerged arc welding;  surfacing welding
分类号:
TG113
DOI:
10.19291/j.cnki.1001-3938.2016.08.004
文献标志码:
A
摘要:
CAP1000机组反应堆压力容器堆测接管管座采用低合金钢埋弧堆焊焊接成型。为了保证堆焊结构的组织和性能的各向同性，使用与CAP1000产品堆测接管管座完全相同的材料以及焊接工艺进行焊接模拟，并从堆焊结构的三个方向，即垂直于焊接方向、平行于焊接方向、堆焊结构的高度方向分别进行拉伸和冲击试验。试验结果表明，采用堆焊方法制作的堆测接管管座具有良好的组织性能，焊接工艺性能优良，未发现焊接缺陷；三个方向的拉伸性能和冲击性能基本相当。
Abstract:
CAP1000 reactor pressure vessel tube socket is made of low alloy steel by submerged arc surfacing welding, in order to ensure the isotropic of microstructure and property for surfacing structure, it used the same material and welding process with CAP1000 products pressure vessel tube socket to simulate welding, and to perform tensile and impact test from three directions, including perpendicular to welding direction, parallel to welding direction, and the welding structure height direction. Test results showed the pressure vessel tube socket made by surfacing welding is with good organization performance, good welding performance, found no weld defects; the tensile and impact properties from three directions are equivalent.

参考文献/References:

[1] 贺振宇，沈伟，姜述杰，等． AP1000机组反应堆压力容器堆测管焊接工艺的研究[J]． 热加工工艺，2015（21）： 172-174，177．
[2] 周志军，侯淑芳． 埋弧自动堆焊工艺参数的确定[J]． 南通航运职业技术学院学报，2006（4）：86-90．
[3] 刘铁军，刘贵强，袁广，等. 埋弧堆焊技术在油缸生产中的应用研究[J]． 煤矿机械，2012（1）：124-126．
[4] 丛高伟，张忠海． 几种压水堆反应堆压力容器结构的比较与研究[J]． 科技创新与应用，2015（20）：123.
[5] 周新华，陈富彬，陈中灼． AP1000反应堆压力容器的制造难点与监造应对措施[J]. 锅炉制造，2015（2）：48-53.
[6] 丁冬平，刘顺洪，周龙早． 基于焊接的快速成形技术[J]．电焊机，2004（6）：30-35．
[7] 杨国明．近净成形技术发展概况[J]． 材料导报，1993（2）：6-7．
[8] 张禹，王世龙，罗震，等． 基于机器人堆焊增材制造工艺与方法研究[J]. 制造业自动化，2013（6）：145-147.
[9] 关桥． 焊接/连接与增材制造（3D打印）[J]． 焊接，2014（5）：1-8．
[10] 耿海滨，熊江涛，黄丹，等． 丝材电弧增材制造技术研究现状与趋势[J]． 焊接，2015（11）：24-28，76．

备注/Memo

备注/Memo:
收稿日期： 2016-05-18
作者简介： 张俊宝（1976—），男，硕士，高级工程师，主要从事核电设备的焊接设计工作。
更新日期/Last Update: