[1]李小龙,张军平,任永峰,等.两种金属化合物对喹啉季铵盐缓蚀性能的影响[J].焊管,2017,40(8):8-11.[doi:10.19291/j.cnki.1001-3938.2017.08.002]
　LI Xiaolong,ZHANG Junping,REN Yongfeng,et al.Influence of Two Kinds of Metal Compounds on Corrosion Inhibition Performance of Quinolone Quaternary Ammonium Salt[J].,2017,40(8):8-11.[doi:10.19291/j.cnki.1001-3938.2017.08.002]
点击复制

两种金属化合物对喹啉季铵盐缓蚀性能的影响
分享到：

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
40
期数:
2017年第8期
页码:
8-11
栏目:
试验与研究
出版日期:
2017-08-28

文章信息/Info

Title:
Influence of Two Kinds of Metal Compounds on Corrosion Inhibition Performance of
Quinolone Quaternary Ammonium Salt
文章编号:
10.19291/j.cnki.1001-3938.2017.08.002
作者:
李小龙1; 2; 张军平3; 任永峰1; 2; 晁利宁1; 2; 苑清英1; 2
1. 国家石油天然气管材工程技术研究中心， 陕西 宝鸡 721008；
2. 宝鸡石油钢管有限责任公司 钢管研究院， 陕西 宝鸡 721008；
3. 西北工业大学 理学院应用化学系， 西安 710129
Author(s):
LI Xiaolong1; 2;  ZHANG Junping3;  REN Yongfeng1; 2;  CHAO Lining1; 2;  YUAN Qingying1; 2
1. Chinese National Engineering Research Center for Petroleum and Natural Gas Tubular Goods, Baoji 721008, Shaanxi, China;
2. Steel Pipe Research Institute, Baoji Petroleum Steel Pipe Co., Ltd., Baoji 721008, Shaanxi, China;
3. Department of Applied Chemistry, School of Natural and Applied Sciences, Northwestern Polytechnical University, Xi’an 710129, China
关键词:
喹啉季铵盐; Al2O3; Al2O3+CuCl2; 缓蚀剂; 复配
Keywords:
quinolone quaternary ammonium salt; Al2O3; Al2O3+CuCl2; corrosion inhibition; compound
分类号:
TG174.42
DOI:
10.19291/j.cnki.1001-3938.2017.08.002
文献标志码:
A
摘要:
为了提高喹啉季铵盐对N80钢的缓蚀性能，采用静态失重法和动电位极化曲线法，研究了在90 ℃、15%HCl溶液中添加Al2O3及Al2O3+CuCl2对喹啉季铵盐缓蚀性能的影响。试验结果显示，160 ℃温度下合成的喹啉季铵盐缓蚀效果较差，不能满足SY/T 5405—1996中的一级指标要求；Al2O3的加入能有效提高喹啉季铵盐对N80钢的缓蚀效果，并且能大大降低喹啉季铵盐的用量；Al2O3+CuCl2和喹啉季铵盐复配后，能更大程度上提高喹啉季铵盐的缓蚀效果，缓蚀性能明显好于Al2O3与喹啉季铵盐形成的复配缓蚀剂。结果表明，喹啉季铵盐能与金属离子形成较为稳定的螯合物，螯合物通过化学作用吸附在挂片表面形成一层致密的铜膜，阻止了腐蚀离子向金属表面移动，从而表现出较好的缓蚀效果。
Abstract:
In order to increase the corrosion inhibition performance of quinolone quaternary ammonium salt on N80 steel, the effect of Al2O3 and Al2O3+CuCl addition on the corrosion inhibition performance of quinoline quaternary ammonium salt in 15%HCl solution at 90 ℃was investigated, by using static weight loss method and polarization curve method. Test results showed that synthesis of quinoline quaternary ammonium salt corrosion inhibition effect at 160 ℃ is poorer, cannot meet the highest level requirement of SY/T 5405—1996 standard; the addition of Al2O3 can effectively enhance the corrosion inhibition effect of quinoline quaternary ammonium salt for N80 steel, and it can greatly reduce the dosage of quinoline quaternary ammonium salt; the compound of Al2O3+CuCl2 and quinoline quaternary ammonium salt can enhance the corrosion inhibition effect of quinoline quaternary ammonium salt to a greater extent, which is obviously better than that of the complex inhibitor from Al2O3 and quinoline quaternary ammonium salt. The results indicated that quinoline quaternary ammonium salt and metal ion can form stable chelates, the chelates is adsorbed by chemical action to form a dense copper film on the hanging surface, which prevents the corrosion ion from moving to the metal surface, thus showing a better corrosion inhibition effect.

参考文献/References:

[1] 李谦定，李恒娟，卢永斌. 咪唑啉季铵盐缓蚀剂的合成及应用性能评价[J]. 西安石油大学学报（自然科学版）， 2011，26（2）：76-79.
[2] 陈蕊，李善建，冯拉俊. 喹啉缓蚀剂对N80石油管道钢小孔腐蚀的影响[J]. 焊管，2013,36（11）：15-19.
[3] 王红艳，卢永斌，白方林，等. 一种新型Mannich 碱酸化 缓蚀剂的合成及性能评价[J]. 2013，25（2）：133-137.
[4] 雷晓维，张娟涛，白真权. 喹啉季铵盐酸化缓蚀剂对超级13Cr不锈钢电化学行为的影响[J]. 腐蚀科学与防护技术，2015，27（4）：358-362.
[5] 蒋平，赵力云，万朝晖，等. 喹啉型季铵盐缓蚀性能评价[J]. 油田化学，2011，28（2）：219-223.
[6] 李恒娟. 高温盐酸缓蚀剂合成及应用研究[D]. 西安：西安石油大学,2011.
[7] 梁丽. 季铵盐型缓蚀剂的合成及性能评价[J]. 化学工程，2010，38（10）：235-237.
[8] 李善建，冯拉俊，董晓军，等. 喹啉与硫脲在含饱和CO2气井采出水中的协同效应[J]. 天然气工业，2015（5）：90-97.
[9] 李小龙, 张军平, 毕宗岳, 等.  一种新型复配酸化缓蚀剂对N80钢的缓蚀性能的影响[J]. 焊管，2016，39（6）：5-9.
[10] 曹楚南. 腐蚀电化学[M]. 北京: 化学工业出版社, 1984.
[11] 程玉峰，杜元龙，曹楚南，等. Na2SO4溶液中磷酸环己胺的缓蚀机理及其吸附与脱附行为[J]. 中国腐蚀与防护学报，1997，12（2）：142-146.
[12] 梅平，霍松，艾俊哲，等. 双喹啉季铵盐在盐酸体系中的缓蚀性能及协同增效作用研究[J]. 化学与生物工程，2010，27（12）：12-14.
[13] 张漫路，赵景茂. 缓蚀剂协同效应与协同机理的研究进展[J]. 中国腐蚀与防护学报，2016, 36（1）：1-10.

相似文献/References:

[1]李小龙,等.一种新型复配酸化缓蚀剂对N80钢缓蚀性能的影响[J].焊管,2016,39(6):5.[doi:10.19291/j.cnki.1001-3938.2016.06.002]
　LI Xiaolong,ZHANG Junping,BI Zongyue,et al.Influence of the Corrosion Inhibition Performance of a New Composite Acidizing Corrosion Inhibitor to N80 Steel[J].,2016,39(8):5.[doi:10.19291/j.cnki.1001-3938.2016.06.002]

备注/Memo

备注/Memo:
收稿日期：2017-05-08
基金项目：国家科技支撑计划“高强度耐蚀石油天然气集输与输送用管线钢生产技术”（项目号2011BAE25B03）。
作者简介：李小龙（1988—），男，硕士，工程师，主要从事石油管材新产品开发及腐蚀与防护研究。
更新日期/Last Update: