油气集输用2205/X65双金属冶金复合管材及焊接工艺()
分享到：

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
41
期数:
2018年第3期
页码:
17-23
栏目:
试验与研究
出版日期:
2018-03-28

文章信息/Info

Title:
2205/X65 Bimetal Metallurgy Composite Pipe and Welding Process for
 Oil and Gas Gathering and Transferring
文章编号:
10.19291/j.cnki.1001-3938.2018.03.004
作者:
刘海璋1; 2; 毕宗岳1; 2; 杨　军1; 2; 牛　辉1; 2; 田　磊1; 2; 杨耀彬1; 2; 孙少阳1; 2
1. 国家石油天然气管材工程技术研究中心，陕西 宝鸡 721008；
2. 宝鸡石油钢管有限责任公司，陕西 宝鸡 721008
Author(s):
LIU Haizhang1;  2;  BI Zongyue1;  2;  YANG Jun1;  2;  NIU Hui1;  2;  TIAN Lei1;  2;  YANG Yaobin1;  2;  SUN Shaoyang1;  2
1. Chinese National Engineering Technology Research Center for Petroleum and Natural Gas Tubular Goods, Baoji 721008, Shaanxi, China;
2. Baoji Petroleum Steel Pipe Co., Ltd.,Baoji 721008, Shaanxi, China
关键词:
2205/X65复合板; TIG+MAG焊; 组织性能; 晶间腐蚀
Keywords:
2205/X65 composite plate;  TIG+MAG welding;  structure property;  intergranular corrosion
分类号:
TE973.3
DOI:
10.19291/j.cnki.1001-3938.2018.03.004
文献标志码:
B
摘要:
为了提高油气田集输管道的抗腐蚀性能，开发了2205/X65双金属冶金复合板，设计了复合管TIG+MAG组合焊接工艺，制备了Φ610 mm×16( 2+14 ) mm 大直径2205/X65双金属复合管，并对复合板材及管材的力学性能、微观组织、耐腐蚀性进行了试验研究。结果表明，复合板材及管材的金相组织、夏比冲击、拉伸、剪切、DWTT、正反弯曲等指标满足相关标准要求；复合管理化性能和抗晶间腐蚀性能满足相关标准要求，可满足含H2S和CO2等腐蚀介质的油气集输要求。
Abstract:
In order to improve the anti-corrosion resistance of pipe for oil and gas gathering and transferring, 2205/X65 bimetal composite plate was developed, the TIG+MAG welding process of composite pipe was designed, the large diameter 2205/X65 Φ610 mm×16(2+14) mm bimetal composite pipe was prepared, and mechanical properties, microstructure and anti-corrosion resistance of composite plate and pipe were tested. The results showed that the microstructure, charpy impact, tensile, shear and DWTT, front and reverse bending, and some other mechanical properties of composite plate met the requirements of relevant standards; the physical and chemical properties and intergranular corrosion resistance of the compound pipe met the requirements of relevant standards, which could meet the requirements of oil and gas gathering and transferring with H2S and CO2 corrosion medium.

参考文献/References:

[1] 吴玖. 双相不锈钢[M]. 北京: 冶金工业出版社, 1999.
[2] 霍春勇，李为卫，熊庆人. 2205双相不锈钢[M]. 西安: 陕西科学技术出版社, 2006.
[3] 刘建彬, 韩静涛, 鲍善勤, 等. 热处理对双金属复合管X65/2205组织及力学性能的影响[J]. 热加工工艺, 2009, 38(4）: 125-127.
[4] 毕宗岳, 丁宝峰, 张峰，等. 2205/Q235大面积双相不锈钢复合板性能分析[J]. 焊管, 2010, 33(3）: 25-28.
[5] 王文先, 王峰, 刘满才, 等. 1Cr18Ni9Ti+Q235复合钢板对接焊缝组织和抗腐蚀性能分析[J]. 焊接学报, 2010, 31(6）: 89-92.
[6] 陈军. 20+304不锈钢复合管的焊接[J]. 江西石油化工, 2005, 17（1）: 40-42.
[7] 孙树山, 杨利娜, 秦增伟, 等. L245NB+316L小管径复合钢管焊接工艺研究[J]. 焊接与切割, 2009(14）: 43-45.
[8] 郭晶，赵云有，车菊秋. 国内复合钢板产品焊接中存在问题分析[J]. 石油化工设备, 2008, 31（1）: 17-19.
[9] 刘政军, 徐德昆. 不锈钢焊接及质量控制[M]. 北京: 化学工业出版社, 2009.
[10] CLEITON C, HELIO C, MIRANDA D, et al. Microstru- cture, hardness and petroleum corrosion evaluation of 316L /AWSE309Mol weldmetal[J]. Materials Characte-rization, 2009, 60（1）: 346-352.
[11] 胡永碧, 谷坛. 高含硫气田腐蚀特征及腐蚀控制技术[J]. 天然气工业, 2012, 32(12）: 92-95.
[12] 李冬玲, 乔雪璎, 刘庆斌, 等. GH4199镍基高温合金的析出相分析研究[J]. 冶金分析, 2005, 25(1）:1-6.

相似文献/References:

[1]毕宗岳.2205/X65冶金复合管材焊接工艺及焊缝组织性能研究[J].焊管,2019,42(2):1.[doi:10.19291/j.cnki.1001-3938.2019.2.001]
　BI Zongyue,Welding Process and Microstructure and Mechanical Property of Butt Joints of 2205/X65 Metallurgical Clad Pipe[J].,2019,42(3):1.[doi:10.19291/j.cnki.1001-3938.2019.2.001]

备注/Memo

备注/Memo:

收稿日期： 2018-01-11

基金项目： 国家863项目课题“双金属层状结构复合管材技术研究”（项目编号2013AA031303）。
作者简介： 刘海璋（1976—），男，陕西宝鸡人，高级工程师，从事油气输送管材开发及焊接工艺研究工作。

更新日期/Last Update: 2018-04-18