感应加热弯管整体淬火工艺对冲击性能的影响
分享到：

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
36
期数:
2013年第4期
页码:
34-36
栏目:
工艺与设备
出版日期:
2013-04-28

文章信息/Info

Title:
Influence of Whole Quenching Process of Induction Heating Bend on Impact Performance
文章编号:
１００１－３９３８（２０１3）04-0034-03
作者:
杨玮玮1; 曹雅彬2; 张海波3; 彭立山3; 赵志伟3
（1. 渤海装备研究院钢管研究所，河北 青县062658；
2. 石家庄铁道大学，石家庄050043；
3. 渤海装备巨龙钢管公司, 河北 青县062658）
Author(s):
YANG Weiwei1;  CAO Yabin2;  ZHANG Haibo3; PENG Lishan3; ZHAO Zhiwei3
（1.CNPC Bohai Equipment Research Institute Steel Pipe Research Institute, Qingxian 062658, Hebei， China；
2. Shijiazhuang Tiedao University, Shijiazhuang 050043， China；
3. CNPC Bohai Equipment Julong Steel Pipe Co., Ltd., Qingxian 062658， Hebei, China）
关键词:
关键词：感应加热弯管; 整体淬火; X80钢
Keywords:
Key words: induction heating bend;  whole quenching;  X80 steel
分类号:
TG156.3
DOI:
１００１－３９３８（２０１3）04-0034-03
文献标志码:
B
摘要:
针对高钢级感应加热弯管，对其整体淬火工艺之后的性能进行了研究，并与局部淬火后的焊缝冲击韧性进行了详细对比，指出了整体淬火工艺的优越性，进一步明确了回火工艺的最佳工艺区间，并对X80钢级感应加热弯管的生产提出了建议。试验结果表明，与局部回火工艺相比，淬火+回火工艺可以有效提高直管段焊缝的冲击韧性，减小直管段与弯曲段的性能差异, 对于X80钢级弯管的淬火+回火工艺来说，最佳工艺区间为550～600 ℃。
Abstract:
Aiming at high grade induction heating bend , it studied the properties after the whole quenching process, detailedly compared the properties with the impact toughness of weld after section part quenching, and put forward the advantage of the whole quenching process. It also further defined the optimal process range in tempering process, and gave some opinions and suggestions for X80 grade induction heating bend production. The test results showed that compared with the section part tempering process, the quenching+tempering process can effectively improve the toughness of weld in straight pipe section, and reduce the performance difference between straight pipe and bend. For quenching+tempering process of X80 grade bend, the optimal process range is 550～600 ℃.

参考文献/References:

［1］ 王晓香，李延丰. 高强度管线钢管开发在中国的新进展［J］.钢管，2011（01）：12-18.
［2］ 李为卫，刘迎来，王长安.西气东输管道弯管的国内外生产工艺对比［J］. 油气储运，2003（12）：21-24.
［3］ GB 2106—1980，金属夏比（V型缺口）冲击试验方法［S］.
［4］ Q/SY GJX 0129—2008，西气东输二线管道工程用感应加热弯管技术条件［S］.
［5］ 王永胜，赵玉鹏，金永英，等.西气东输二线X80热煨弯管研制［J］.热加工工艺，2012（19）：122-123.
［6］ 孔君华.高钢级X80管线钢工艺、组织与性能的研究［D］.武汉：华中科技大学，2005.
［7］ 赵志伟，徐强，彭立山，等.X80感应加热弯管回火工艺研究［J］.焊管，2012（01）：44-47.

备注/Memo

备注/Memo:
—————————
作者简介：杨玮玮（1982—），工程师，2008年毕业于大连理工大学材料专业，硕士学历，现主要从事焊接材料与焊接工艺的研究工作。
更新日期/Last Update: