超宽X70M钢板的超快冷工艺及产品性能研究()

分享到：

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

Title:: Study on Ultra-fast Cooling Process and Product Properties of Ultra-wide X70M Steel Plate

Author(s):: QU Zhiguo; LIU Zhenhua; YANG Haifeng; Minmetals YingKou Medium Plate Co., Ltd., Yingkou 115000, Liaoning, China

Keywords:: X70M steel plate; ultra-wide; ultra-fast cooling; mechanical property

摘要:: 为了满足某超宽规格高钢级管线钢板出口项目要求，通过优化成分设计及冶炼轧制工艺，采用UFC超快冷工艺开发了厚度19.7～22.2 mm、宽度4 376 mm的超宽X70M管线钢板，并实现了稳定生产。对批量生产的钢板进行了力学性能试验，试验结果显示，钢板屈服强度均值552 MPa，抗拉强度均值646 MPa，屈强比均值0.85%，-30 ℃冲击功均值＞300 J，-15 ℃ DWTT剪切面积均值92%。研究表明，开发的4 376 mm超宽X70M钢板满足制管要求。

Abstract:: In order to meet the requirements of an ultra-wide high grade pipeline steel plate export project, ultra-wide X70M pipeline steel plate with thickness of 19.7~22.2 mm and width of 4 376 mm was developed by UFC ultra-fast cooling process through optimizing composition design and smelting rolling process, and stable production was realized. The results show that the average yield strength is 552 MPa, the average tensile strength is 646 MPa, the average yield strength ratio is 0.85%, the average impact energy at -30 ℃ is more than 300 J, and the average shear area of DWTT at -15 ℃ is 92%. The research shows that the developed 4 376 mm ultra-wide X70M steel plate meets the requirements of pipe making.

[1] 王晓香. 国内外超大输量天然气管道建设综述[J]. 焊管，2019，42（7）：1-9.

[2] 毕宗岳. 新一代大输量油气管材制造关键技术研究进展[J]. 焊管，2019，42（7）：10-25.

[3] 张振永. 中俄东线X80钢级Φ1 422 mm管道工程设计关键技术应用[J]. 焊管，2019，42（7）：64-71.

[4] 刘丹，陈俊奇，温冰. 超宽管线钢X70的轧制工艺研究[J]. 宽厚板，2010,16（1）：18-20.

[5] 张飘飘，镇凡，邵伟，等. 轧制工艺对X70级管线钢组织与性能的影响[J]. 金属热处理，2018，43（6）：201-206.

[6] 李群，王志勇，田鹏，等. 中厚板TMCP工艺品种钢板形控制策略研究[J]. 轧钢，2014，31（5）：20-22.

[7] 高惠临. 管线钢与管线钢管[M]. 北京：中国石化出版社，2012.

[8] 章传国，翟启杰，郑磊. 板坯加热工艺对厚规格管线钢组织性能的影响[J]. 钢铁，2018，53（3）：76-81.

[9] 张志波，刘清友，张晓兵，等. 加热温度对管线钢奥氏体晶粒尺寸和铌固溶的影响[J]. 钢铁研究学报，2008，20（10）：36-39.

更新日期/Last Update: 2021-05-18