[1]王一非,石张泽,张学智,等.某生产井定位密封穿孔失效原因分析[J].焊管,2022,45(2):44-48,52.[doi:10.19291/j.cnki.1001-3938.2022.02.007]
　WANG Yifei,SHI Zhangze,ZHANG Xuezhi,et al.Failure Analysis of Positioning Seal Perforation in Production Well[J].,2022,45(2):44-48,52.[doi:10.19291/j.cnki.1001-3938.2022.02.007]
点击复制

某生产井定位密封穿孔失效原因分析()
分享到：

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
45
期数:
2022年第2期
页码:
44-48,52
栏目:
失效分析
出版日期:
2022-02-28

文章信息/Info

Title:
Failure Analysis of Positioning Seal Perforation in Production Well
文章编号:
10.19291/j.cnki.1001-3938.2022.02.007
作者:
王一非; 石张泽; 张学智; 冯电稳; 杨中娜; 杨 阳
1. 中海油能源发展股份有限公司工程技术分公司，天津 300452；2. 中海石油（中国）有限公司天津分公司，天津 300459；3. 中海油（天津）管道工程技术有限公司，天津 300452；4. 天津北海油人力资源咨询服务有限公司，天津 300452
Author(s):
WANG Yifei;  SHI Zhangze;  ZHANG Xuezhi;  FENG Dianwen;  YANG Zhongna;  YANG Yang
1.Engineering Technology Branch of CNOOC Energy Development Co., Ltd., Tianjin 300452, China;2. Tianjin Branch of China National Offore Oil Co., Ltd., Tianjin, 300459, China; 3.CNOOC (Tianjin) Pipeline Engineering Technology Co., Ltd., Tianjin 300452, China; 4. Tianjin North CNOOC Human Resources Consulting Service Co., Ltd., Tianjin 300452, China
关键词:
井下管柱; 定位密封; 冲刷腐蚀; 失效分析
Keywords:
downhole string;  positioning seal;  erosion corrosion;  failure analysis
分类号:
TG172
DOI:
10.19291/j.cnki.1001-3938.2022.02.007
文献标志码:
B
摘要:
针对某油田生产井起出井下管柱作业时发现定位密封处发生穿孔现象，通过宏观分析及测量、理化性能分析、显微组织观察、腐蚀行为分析等方法，对该井定位密封失效原因进行研究。结果表明，短节与油管的化学成分检测结果均满足API SPEC 5CT标准对N80的要求，而定位密封各部位材质不一致，分别为1Cr、13Cr材质，且13Cr材质硬度较高；含砂采出液经油管进入定位密封内部后，受扩径紊流影响，介质集中对定位密封底部形成冲刷，由于13Cr材质耐磨性、耐蚀性均优于1Cr材质，导致1Cr材质冲刷腐蚀严重，进而发生穿孔。建议严格控制管柱各部位材料质量，控制采出液中含砂量及CO2含量，以预防该类失效的再次发生。
Abstract:
In view of the perforation at the positioning seal found in the downhole string operation of a production well in an oil field, the failure causes of the positioning seal of the well are studied by macro analysis and measurement, physical and chemical performance analysis, microstructure observation and corrosion behavior analysis. The results show that the chemical composition test results of nipple and tubing meet the requirements of API SPEC 5CT standard for N80, while the materials of various parts of positioning seal are inconsistent, which are 1Cr and 13Cr respectively, and 13Cr has high hardness. After the sand bearing produced fluid enters the positioning seal from the oil pipe, affected by diameter expansion turbulence, the medium concentration scours the bottom of the positioning seal. Because the wear resistance and corrosion resistance of 13Cr material are better than that of 1Cr material, the erosion corrosion of 1Cr material is serious, and then perforation occurs. It is suggested to strictly control the material quality of each part of the string, and control the sand content and CO2 content in the produced fluid, so as to prevent the recurrence of such failure.

参考文献/References:

[1] 钟彬，陈义庆，孟凡磊，等. N80油管穿孔失效原因分析[J]. 腐蚀与防护，2018，39（8）：647-650.[2] 张帅，杨阳，金磊，等. 某油田注水井油管腐蚀失效分析[J]. 石油化工腐蚀与防护，2020，37（3）：58-61.[3] 刘磊，杨阳，罗懿. 某生产井旁通管断裂失效分析[J]. 化工装备技术，2020，41（3）：19-23.[4] 姚彬，郭玉洁，曾文广，等. 塔河油田某注采井生产油管腐蚀失效分析[J]. 石油与天然气化工，2019，48（4）：69-73..[5] 王雪，夏晞冉，秦永光，等. 油气田设备多相流冲蚀磨损主控因素研究进展[J]. 安全、健康和环境，2021，21（5）：1-6.[6] 王海红，王平，闫龚杰，等. N80套管钢在液固两相流中的冲刷腐蚀行为[J]. 石油工程建设，2021，47（1）：10-14.[7] 张晓东，贾国超，吴臣德. 空气钻井钻具冲蚀磨损机理的分析[J]. 西南石油大学学报(自然科学版)，2009，31（2）：139-142.[8] 练章华，魏臣兴，宋周成，等. 高压高产气井屈曲管柱冲蚀损伤机理研究[J]. 石油钻采工艺，2012，34（1）：6-9.[9] 董刚，张九渊. 固体粒子冲蚀磨损研究进展[J]. 材料科学与工程学报，2003（2）：307-312.[10] 陈海龙，杨学锋，鹿重阳，等. 固体粒子冲蚀磨损理论及影响因素的研究概述[J]. 材料导报，2017，31（S2）：403-406.[11] 孟庆武，韩文静，王宪明，等. 油管材料在砂油水液条件下的冲蚀磨损性能[J]. 石油矿场机械，2008（2）：52-54.[12] 安杰. 油气井管柱受颗粒冲蚀的数值模拟[D]. 荆州：长江大学，2014.[13] 杨向同，周鹏遥，丁亮亮，等. P110油管用钢液固两相流体冲蚀实验研究[J]. 科学技术与工程，2014，14（30）：140-143.[14] 吕洪亮. 油田注水管线腐蚀结垢成因的药剂控制技术[J]. 化学工程与装备，2020（8）：101-102.[15] 李荣强. 胜利油田注水管柱腐蚀机理与防治技术[J]. 石油钻探技术，2008（4）：64-66.

相似文献/References:

[1]张继刚,陈钦伟,刘洪文,等.某注水井油管穿孔失效原因分析[J].焊管,2021,44(8):36.[doi:10.19291/j.cnki.1001-3938.2021.08.007]
　ZHANG Jigang,CHEN Qinwei,LIU Hongwen,et al.Failure Analysis of Tubing Perforation in a Water Injection Well[J].,2021,44(2):36.[doi:10.19291/j.cnki.1001-3938.2021.08.007]

备注/Memo

备注/Memo:
收稿日期：2021-08-13作者简介：王一非（1985—），男，工程师，主要从事修井及井筒工艺相关研究工作。
更新日期/Last Update: 2022-03-03