集输油用非金属柔性复合管研制与性能评价()
分享到：

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
46
期数:
2023年第7期
页码:
64-70
栏目:
试验与研究
出版日期:
2023-07-19

文章信息/Info

Title:
Development and Performance Evaluation of Non?etallic Flexible Composite Pipes for Oil Gathering and Transportation
文章编号:
10.19291/j.cnki.1001-3938.2023.07.009
作者:
毕宗岳; 刘德俊; 孙文盛; 张阿昱; 刘亚明; 梁航; 赵苗苗
1. 中油国家石油天然气管材工程技术研究中心有限公司，西安 710018； 2. 中国石油宝鸡石油钢管有限责任公司，陕西 宝鸡 721008； 3. 陕西省高性能连续管重点试验室，陕西 宝鸡 721008
Author(s):
BI Zongyue;  LIU Dejun;  SUN Wensheng;  ZHANG Ayu;  LIU Yaming;  LIANG Hang;  ZHAO Miaomiao
1. Chinese National Engineering Research Center for Petroleum and Natural Gas Tubular Goods Co., Ltd., Xi’an 710018, China; 2. CNPC Baoji Petroleum Steel Pipe Co., Ltd., Baoji 721008, Shaanxi, China; 3. Shaanxi Province Key Laboratory of High Performance Coiled Tubing, Baoji 721008, Shaanxi, China
关键词:
非金属柔性复合管; 介质相容性; 性能评价; 使用寿命
Keywords:
nonmetallic flexible composite pipe;  media compatibility;  performance evaluation;  service life
分类号:
TE977
DOI:
10.19291/j.cnki.1001-3938.2023.07.009
文献标志码:
A
摘要:
针对油气田地面集输管线腐蚀泄露、结蜡堵塞问题，研究开发了一种高性能油气介质相容性好、内压强度高的非金属柔性复合管，并对制备的非金属柔性复合管内衬层进行油品介质相容性试验以及相关力学性能评价。结果表明，在温度70 ℃、压力10 MPa、0号柴油介质下浸泡1 080 h后，内衬管氧化诱导时间（OIT）衰减率为14.3%，远小于普通PE100管材的衰减率（56.9%）；拉伸强度衰减率为8.01%，低于普通PE100管材（18.05%），具有较好的耐介质相容性。对制备的DN50 mm非金属柔性复合管进行评价，爆破压力可达37.2 MPa，在最小弯曲半径600 mm下，全周期循环弯曲10 次未出现开裂，循环后爆破强度为31.2 MPa。通过长期静液压试验预测寿命表明，在40~50 ℃和使用压力为9.6 MPa工况下，该管材可正常服役50年。产品各项性能完全满足GB/T 38725.2—2020和SY/T 6662.2—2020相关要求，为油气田地面集输道提供了新的选择。
Abstract:
For the surface gathering and transportation pipeline in oil and gas field, a non?etallic flexible composite pipe with good compatibility of high?erformance oil and gas medium and high internal pressure strength was researched and developed. The prepared non?etallic flexible composite pipe lining layer was tested for oil medium compatibility and related mechanical property evaluation. The results show that after soaking for 1 080 h at a temperature of 70 °C, pressure of 10 MPa and No. 0 diesel, the attenuation rate of oxidation induction time (OIT) of lined pipe is 14.3%, which is much lower than that of ordinary PE100 pipe (56.9%). The tensile strength attenuation rate is 8.01%, which is lower than that of ordinary PE100 pipe (18.05%), and has good media compatibility. The evaluation of the prepared DN50 mm non?etallic flexible composite pipe, the bursting pressure can reach 37.2 MPa, under the minimum bending radius of 600 mm, the whole cycle is bent 10 times without cracking, and the bursting strength after the cycle is 31.2 MPa, and the predicted life through long?erm hydrostatic test shows that the pipe can serve normally for 50 years under the working conditions of 40~50 °C and use pressure of 9.6 MPa. The performance of this product fully meets the relevant requirements of GB/T 38725.2—2020 and SY/T 6662.2—2020, providing a new choice for oil and gas field surface gathering and transportation pipelines.

参考文献/References:

［1］ 羊东明，葛鹏莉，朱原原.塔河油田苛刻环境下集输管线腐蚀防治技术应用［J］.表面技术，2016，45（2）：57-64.［2］ 张兆，刘鹏，徐超，等.玻璃纤维增强热塑性复合管性能评价方法研究进展［J］.中国塑料，2019，33（8）：136-143.［3］ 赵晓云，毛志高，朱名昭，等.油田集输管道内腐蚀直接评价技术及实践应用［J］.全面腐蚀控制，2019，33（4）：1-5，61.［4］ 董绍华，王东营，董国亮，等.管道内腐蚀直接评估技术与实践应用［J］.石油科学通报，2016，1（3）：459-470.［5］ 丁东升.输油管道腐蚀问题与防护措施研究［J］.全面腐蚀控制，2021，35（6）：134-135.［6］ 何慧.油田采出水输送管道的选材分析［J］.中国石油大学胜利学院学报，2019，33（4）：35-38.［7］ 郭连升，王振东.柔性复合高压输送管在油田开发中的应用［J］.清洗世界，2020，36（7）：103-104.［8］ 闫治国，张骁勇，魏斌，等.纤维缠绕增强柔性复合管研究现状与发展趋势［J］.云南化工，2021，48（2）：22-24，27.［9］ 张冠军，齐国权，戚东涛.非金属及复合材料在石油管领域应用现状及前景［J］.石油科技论坛，2017，36（2）：26-31，37.［10］ 于柏峰.油气输送用柔性增强热塑性管道研究和应用［J］.纤维复合材料，2018，35（4）：29-33，12.［11］ 孙哲，孙振国，刘惠明，等.柔性增强热塑性塑料管道的发展和市场前景［J］.新型建筑材料，2013，40（12）：97-101.［12］ 李晓平，李愚，王茀玺，等.非金属复合材料管道综述［J］.石油工业技术监督，2017，33（10）：1-4.［13］ 乔霭潼.纤维缠绕增强复合管在内压作用下的力学行为研究［D］.杭州：浙江大学，2014.［14］ 国家能源局.石油天然气工业用非金属复合管 第2部分：柔性复合高压输送管：SY/T 6662.2—2012［S］.北京：石油工业出版社，2012.［15］ 中华人民共和国国家质量监督检疫检验总局.可盘绕式增强塑料管 第2部分：纤维增强热塑性塑料连续管：GB/T 38725.2—2020［S］.北京：中国标准出版社，2020.［16］ 李敏，张启跃.橡胶工业手册［M］.北京：化学工业出版社，2012.［17］ 江云涛，黄佃平，邵华峰，等.结晶度对聚丁烯-1力学性能的影响［J］.现代塑料加工应用，2008，20（1）：26-29.［18］ 杨素，杨苏平，陈枫.聚乙烯短支链与其结晶度关系的定量研究［J］.现代塑料加工应用，2006，18（2）：33-35.［19］ 代军，晏华，郭骏骏，等.结晶度对高密度聚乙烯热氧老化特性的影响［J］.高分子材料科学与工程，2016，32（9）：65-71.［20］ 梁基照.HDPE熔融热焓与结晶度的测定［J］.广州化工，1994，22（4）：17-30.［21］ 齐国权，戚东涛，李循迹，等.PET纤维增强柔性复合管耐高温性能实验［J］.油气储运，2015， 34（6）：616-620.［22］ 李风，张绍东，王观军，等.玻纤带增强黏合型HDPE内衬柔性复合管性能试验研究［J］.塑料工业，2021，49（S1）：74-77.［23］ 韩方勇，吴浩，张松.非金属复合管压力等级简化评定方法［J］.油气与新能源，2021，33（6）：58-62.

备注/Memo

备注/Memo:
收稿日期：2022-09-25
基金项目： 中国石油集团公司重大科技专项“油田用复合管新材料的开发及应用”（项目编号2020E-2801J）。
作者简介：刘德俊（1989—），男，硕士研究生，工程师，主要从事非金属管材研究开发工作。
更新日期/Last Update: 2023-07-19