[1]刘世程,刘文红,林 凯,等.316L/30Mn2冶金复合油管的开发与力学性能检测[J].焊管,2022,45(5):36-40.[doi:10.19291/j.cnki.1001-3938.2022.05.005]
　LIU Shicheng,LIU Wenhong,LIN Kai,et al.Development and Mechanical Properties Test of 316L/30Mn2 Metallurgical Composite Tubing[J].,2022,45(5):36-40.[doi:10.19291/j.cnki.1001-3938.2022.05.005]
点击复制

316L/30Mn2冶金复合油管的开发与力学性能检测()
分享到：

《焊管》[ISSN:1001-3938/CN:61-1160/TE]

卷:
45
期数:
2022年第5期
页码:
36-40
栏目:
应用与开发
出版日期:
2022-05-28

文章信息/Info

Title:
Development and Mechanical Properties Test of 316L/30Mn2 Metallurgical Composite Tubing
文章编号:
10.19291/j.cnki.1001-3938.2022.05.005
作者:
刘世程; 刘文红; 林 凯; 宋玉春
1. 大连交通大学 材料科学与工程学院， 辽宁 大连 116028； 2. 中国石油集团工程材料研究院有限公司， 西安 710077； 3. 志杰科技开发（大连）有限公司， 辽宁 大连 116600
Author(s):
LIU Shicheng;  LIU Wenhong;  LIN Kai;  SONG Yuchun
1. School of Materials Science and Engineering, Dalian Jiaotong University, Dalian 116028, Liaoning，China;2. CNPC Tubular Goods Research Institute, Xi’an 710077, China;3. Zhijie Technology Development （Dalian） Co., Ltd., Dalian 116600, Liaoning，China
关键词:
双金属复合油管; 耐蚀合金复合管; 钎焊; 热处理; 界面剪切强度
Keywords:
bimetallic composite tubing;  corrosion resistant alloy composite pipe;  brazing;  heat treatment;  interfacial shear strength
分类号:
TG454
DOI:
10.19291/j.cnki.1001-3938.2022.05.005
文献标志码:
A
摘要:
为研究316L/30Mn2双金属冶金复合油管的制备工艺及力学性能，采用钎焊复合+热处理强化方法，试制了Φ88.9 mm×（6.45+2）mm规格的双金属复合油管，测定了复合油管不同部位的硬度、拉伸、冲击性能和界面剪切强度，并对其技术可行性进行探讨。结果表明，钎焊复合界面冶金结合牢固；适当的热处理使基管、管端接环及对接焊缝的力学性能相近，且在不同热处理工艺下，双金属复合油管基管分别满足80 ksi、95 ksi、110 ksi钢级油管的力学性能要求。该研究进一步验证了开发高性能双金属冶金复合油管的技术可行性，也为双金属复合油管的开发提供依据。
Abstract:
In order to study the preparation process and mechanical properties of 316L/30Mn2 bimetallic metallurgical composite tubing, the brazing composite+heat treatment strengthening method is adopted in trial-producing Φ88.9 mm×（6.45+2） mm bimetallic composite tubing, the hardness, tensile, impact properties and interfacial shear strength of different parts of the composite tubing were measured, and its technical feasibility was discussed. The results show that the bonding interface of brazing is firm. Proper heat treatment makes the mechanical properties of the base pipe, coupling and butt weld similar. Under different heat treatment processes, the base pipe of bimetallic composite tubing meets the mechanical property requirements of 80 ksi, 95 ksi and 110 ksi steel tubing respectively. The study further verifies the technical feasibility of developing high-performance bimetallic metallurgical composite tubing, and also provides a basis for the development of bimetallic composite tubing.

参考文献/References:

[1] 王少兰，费敬银，林西华，等． 高性能耐蚀管材及超级13Cr研究进展[J]. 腐蚀科学与防护技术，2013，25（4）：322-326．[2] 李为卫，秦长毅，贾君君，等. 一种油气田开发用新型双金属复合管[J]. 钢管，2009，38（4）：22-24．[3] 孙育禄，白真权，张国超，等． 油气田防腐用双金属复合管研究现状[J]． 全面腐蚀控制，2011，25（5）：10-13．[4] 曾德智，杜清松，谷坛，等． 双金属复合管防腐技术研究进展[J]． 油气田地面工程，2008，27（12）：64-65．[5] 王纯，毕宗岳，张万鹏，等． 国内外双金属复合管研究现状[J]． 焊管，2015，38（12）：7-12．[6] 王永芳，袁江龙，张燕飞，等． 双金属复合管的技术现状和发展方向[J]． 焊管，2013，36（2）：5-9．[7] 陈丽娟，尚峰，樊学华，等． 海外油田用X52NS/825冶金复合钢管的开发及性能研究[J]． 钢管，2020，49（1）：33-37．[8] 杨专钊，王扬，李安强，等． 双金属复合管分类及其特性分析[J]． 石油管材与仪器，2019，5（1）：1-6．[9] 魏斌，白真权，尹成先，等. 双金属复合管螺纹连接接头：CN201218372[P]. 2009-04-08.[10] 志杰科技开发（大连）有限公司. 可端部螺纹连接的高强度不锈钢复合钢管及其制造方法：CN201710488281.3[P]. 2017-09-22． [11] 王小艳，王斌，杜卫峰，等. 一种冶金式复合油井管及其制造方法：CN107313724A[P]. 2017-11-03.[12] 路彩虹，韩礼红，杨尚谕，等. 一种双金属冶金复合管及其制备方法：CN110181230B[P]. 2022-01-04.[13] 李鹤林，韩礼红，张文利． 高性能油井管的需求与发展[J]. 钢管，2009，38（1）：1-9．[14] 李琼玮，奚运涛，董晓焕，等． 超级13Cr油套管在含H2S气井环境下的腐蚀试验[J]． 天然气工业，2012，32（12）：106-109．

备注/Memo

备注/Memo:
收稿日期：2022-01-05作者简介：刘世程（1948—），男，工学博士，大连交通大学材料学院教授，现主要从事双金属复合材料研究与开发。
更新日期/Last Update: 2022-05-30